根据各种温度条件下低密度聚乙烯(LDPE)和线性低密度聚乙烯(LLDPE)熔体的熔融纺丝测量结果,绘制了拉伸主曲线;比例系数b反映了拉伸过程中的分子链解缠和取向对于熔体拉伸流变性能的综合作用,与温度T呈线性关系;利用b值和参考曲线,对设定温度条件下的拉伸黏度曲线进行了估箅,与实测值吻合良好.主曲线分析扩展了熔融纺丝法的测量范围.
参考文献
| [1] | Liang JZ .Planar entry converging flow during extrusion of polymer melts[J].Polymer-Plastics Technology and Engineering,2007(5):475-480. |
| [2] | LAUN H M;SCHUCH H .Transient elongational viscosities and drawability of polymer melts in rheology[J].Journal of Rheology,1989,33(01):119-175. |
| [3] | REVENU P;GUILLET J;CARROT C .Elongational flow of polyethylenes in isothermal melt spinning[J].Journal of Rheology,1993,37(06):1041-1056. |
| [4] | MUKE S;IVANOV I;KAO N et al.Extensional rheology of polypropylene melts from the rheotens test[J].Journal of Non-Newtonian Fluid Mechanics,2001,101(1-3):77-93. |
| [5] | Baldi F;Franceschini A;Ricco T .Determination of the elongational viscosity of polymer melts by melt spinning experiments. A comparison with different experimental techniques[J].Rheologica Acta: An International Journal of Rheology,2007(7):965-978. |
| [6] | Baldi F;Franceschini A;Bignotti F;Tieghi G;Ricco T .Rheological behaviour of nano-composites based on polyamide 6 under shear and elongational flow at high strain rates[J].Rheologica Acta: An International Journal of Rheology,2009(1):73-88. |
| [7] | WAGNER M H;SCHULZE V;GOTTFERT A .Rheotens-mastercurves and drawability of polymer melts[J].Polymer Engineering and Science,1996,36(07):925-935. |
| [8] | M. H. Wagner;A. Bernnat;V. Schulze .The rheology of the rheotens test[J].Journal of Rheology,1998(4):917-928. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%