利用不同温度的热处理工艺改善510L热轧带钢表面原始氧化皮结构,通过X射线衍射(XRD)、扫描电子显微镜(SEM)、EDS、电化学测试方法对不同结构氧化皮的热轧带钢在NaHSO<,3>溶液中的腐蚀行为进行了研究.结果表明:当温度低于570℃时,随氧化温度的增加,氧化皮上分布的白色弥散状组织减少,氧化皮的微观形貌由带毛刺的小颗粒状演变成针叶状,氧化皮更致密,氧化皮中的Fe<,2>O<,3>的相对含量增加,不同温度制备的热轧带钢氧化皮的耐蚀性由好到差依次为550,500,450,400,350℃.氧化温度介于570℃>T>450℃时,原始氧化皮的耐蚀性可通过热处理得到改善.
参考文献
| [1] | 何爱花 .热轧钢板氧化膜对基体碳钢腐蚀电化学行为的影响[D].中国海洋大学,2007. |
| [2] | R. K. Singh Raman B. Gleeson D. J. Young .Laser Raman spectroscopy: a technique for rapid characterisation of oxide scale layers[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1998(5):373-376. |
| [3] | J. Tiley;Y. Zhang .Hot compression testing of mild steel industrial reheat furnace scale[J].Steel Research,1999(11):437-440. |
| [4] | 齐慧滨,应白桦.钢铁产品的腐蚀与防护[J].世界钢铁,2006(04):29-37. |
| [5] | C. F. Dong;H. B. Xue;X. G. Li;H. B. Qi;Y. F. Cheng .Electrochemical corrosion behavior of hot-rolled steel under oxide scale in chloride solution[J].Electrochimica Acta,2009(17):4223-4228. |
| [6] | F.J. Perez;L. Martinez;M.P. Hierro;C. Gomez;A.L. Portela;G.N. Pucci;D. Duday;J. Lecomte-Beckers;Y. Greday .Corrosion behaviour of different hot rolled steels[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(2):472-480. |
| [7] | 张华,钱余海,齐慧滨,王炜.汽车热轧钢板的锈蚀行为及预防措施[J].腐蚀与防护,2008(06):316-318,333. |
| [8] | 赵迪,姜育男.浅析热轧带钢氧化铁皮表面缺陷的产生及对策[J].本钢技术,2008(01):20-22. |
| [9] | A. Chattopadhyay;N. Bandyopadyay;A. K. Das .Oxide Scale Characterization of Hot Rolled Coils by Raman Spectroscopy Technique[J].Scripta materialia,2005(3):211-215. |
| [10] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001 |
| [11] | 薛会斌 .热轧带钢氧化皮组成与结构对其腐蚀行为的影响[D].北京科技大学,2008. |
| [12] | Lucia Suarez;Yvan Houbaert;Xavier Vanden Eynde;Rafael Colas .High Temperature Deformation Of Oxide Scale[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(2):309-315. |
| [13] | 何爱花,孟洁,王佳,齐慧滨,徐海波.表面氧化膜对B510L热轧钢板腐蚀行为的影响[J].中国腐蚀与防护学报,2008(04):197-200. |
| [14] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004 |
| [15] | 赵旭辉,左禹,赵景茂.几种封闭方法处理后铝阳极氧化膜的耐蚀性比较[J].腐蚀与防护,2006(08):400-403. |
| [16] | Hamadou L;Kadri A;Benbrahim N .Characterisation of passive films formed on low carbon steel in borate buffer solution (pH 9.2) by electrochemical impedance spectroscopy[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(5):1510-1519. |
| [17] | G. K. Glass;A. M. Hassanein;N. R. Buenfeld .Obtaining impedance information on the steel-concrete interface[J].Corrosion: The Journal of Science and Engineering,1998(11):887-897. |
| [18] | 梁平,李晓刚,杜翠薇,陈旭,张亮.溶解氧对X80管线钢在NS4溶液中腐蚀行为的影响[J].腐蚀科学与防护技术,2009(01):20-23. |
| [19] | 李金波,左剑恶.温度和硫离子对N80钢CO2腐蚀电化学行为的影响[J].腐蚀科学与防护技术,2009(01):44-47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%