通过单根Z-pin从复合材料层合板中拔出的试验方法,测试了Z-pin的拔出强度,计算了Z-pin的临界埋入深度,并引入抗拉强度利用率概念来表征Z-pin的抗拉强度在拔出过程中的利用程度.结果表明,直径0.50mm和0.28mm的Z-pin临界埋入深度分别约为5.1mm和3.1mm.当Z-pin的埋入深度小于临界埋入深度时,Z-pin从层板中拔出；Z-pin拔出强度与埋入深度成正比,与Z-pin的直径成反比；当Z-pin的埋入深度大于临界埋入深度时,Z-pin发生断裂,Z-pin的抗拉强度利用率达到100％.最后提出了提高抗拉强度利用率的建议.
参考文献
| [1] | A.P. Mouritz .Review of z-pinned composite laminates[J].Composites, Part A. Applied science and manufacturing,2007(12):2383-2397. |
| [2] | FREITAS G;MAGEE C;DARDZINSKI P et al.Fiber inser tion process for improved damage tolerance in aircraft laminates[J].Journal Advanced Material,1994,25(04):36-43. |
| [3] | Ivana K. Partridge;Denis D.R. Cartie .Delamination resistant laminates by Z-Fiber~R pinning: Part I manufacture and fracture performance[J].Composites, Part A. Applied science and manufacturing,2005(1):55-64. |
| [4] | Denis D.R. Cartie;Manos Troulis;Ivana K. Partridge .Delamination of Z-pinned carbon fibre reinforced laminates[J].Composites science and technology,2006(6):855-861. |
| [5] | LIU H Y;YAN W Y;YU X Y.Experimental study on z-pinned DCB mode Ⅰ delamination[A].Brisbane Australia,2004 |
| [6] | 郑锡涛,李泽江,杨帆.Z-pin增强复合材料层合板断裂韧性试验研究[J].复合材料学报,2010(04):180-188. |
| [7] | 刘(韦华),矫桂琼,管国阳,常岩军.Z-pin增强陶瓷基复合材料拉伸和层间剪切性能[J].复合材料学报,2007(01):86-90. |
| [8] | 韩立军,李铁虎,刘建军,邱海鹏,丁海英.采用Z-Pin增强体的3D炭/炭复合材料层间断裂行为[J].新型炭材料,2004(02):97-102. |
| [9] | McBEATH S .Safety pins[J].Racecar Engineering,2002,12:56-62. |
| [10] | ANONYMOUS.Z pins strengthen the super hornet,save weight and cost[J].The Integrator,2001(03):1-2. |
| [11] | 王晓旭,陈利.复合材料z-pinning技术的应用与发展[J].宇航材料工艺,2009(06):10-14. |
| [12] | FREITAS G;FUSCO T;CAMPBELL T.Z-Fibre technology and products for enhancing composite design[A].Florence,Italy,1996 |
| [13] | 孙先念,郑长良.层合复合材料z-pinning增强技术的力学进展[J].航空学报,2006(06):1194-1202. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%