采用树脂转移模塑(RTM)工艺制备先进复合材料的关键是高性能树脂基体的选择.以N,N’-二氨基二苯甲烷双马来酰亚胺(BDM)、O,O′-二烯丙基双酚A(DBA)和双酚A型氰酸酯(CE)为树脂基体(简称为BD-CE树脂),以超支化聚硅氧烷(HBPSi)为活性稀释剂,开发了适用于RTM工艺的高性能改性树脂体系(mRTM).研究了HBPSi对mRTM树脂的工艺性及其固化树脂的综合性能的影响.结果表明,mRTM树脂的黏度与HBPSi的含量有着直接的关系；mRTM固化树脂的综合性能均明显优于BD-CE树脂.与纯BD-CE树脂相比,mRTM树脂具有良好的反应活性；加入适量的HBPSi后mRTM树脂力学和热学性能显著提高,说明mRTM树脂适宜于通过RTM工艺制备先进结构复合材料.
参考文献
| [1] | Cao HW;Xu RW;Yu DS .Thermal and dielectric properties of bismaleimide-tiriazine resins containing octa(maleimidophenyl)silsesquioxane[J].Journal of Applied Polymer Science,2008(5):3114-3121. |
| [2] | ZHAO JL;FU T;HAN Y et al.Reinforcing hydroxyapatite/thermosetting epoxy composite with 3-D carbon fiber fabric through RTM processing[J].Materials Letters,2004,58(1-2):163. |
| [3] | ZHONGMING LI;MINGBO YANG;RUI HUANG;MEIDONG ZHANG;JIANMIN FENG .Bismaleimide Resin Modified with Diallyl Bisphenol A and Diallyl p-Phenyl Diamine for Resin Transfer Molding[J].Journal of Applied Polymer Science,2001(12):2245-2250. |
| [4] | 张国彬,范晓东,刘郁杨,孔杰,王生杰.紫外光固化超支化聚硅氧烷的合成及其光固化动力学研究[J].高分子学报,2007(07):644-651. |
| [5] | SONG HC.Polymer Composites[M].北京:北京航空航天大学出版社,1985 |
| [6] | CHENG XB.High-Performance Base Body Resin[M].北京:化学工业出版社,1999 |
| [7] | Gu AJ.;Liang GZ. .Thermal degradation behaviour and kinetic analysis of epoxy/montmorillonite nanocomposites[J].Polymer Degradation and Stability,2003(2):383-391. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%