以具有形状记忆特性的改性环氧树脂为基体,通过对其进行纤维增强,制备了一种具有形状记忆特性的炭纤维复合材料.动态机械力学分析(DMA)结果表明,材料具有两个玻璃化转变温度,分别是132℃和223℃.材料的热变形温度确定为两个玻璃化转变温度之间,150℃.在此温度下,可实现材料的变形与回复.材料的形状记忆固定率和形状回复率分别为96-99％和100％,材料的形状回复时间在10分钟之内.
参考文献
| [1] | C.Li;H.Qin;P.T.Mather .Review of progress in shape-memory polymers[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2007(16):1543-1558. |
| [2] | Takeru Ohki;Qing-Qing Ni;Norihito Ohsako .Mechanical and shape memory behavior of composites with shape memory polymer[J].Composites, Part A. Applied science and manufacturing,2004(9):1065-1073. |
| [3] | Ken Gall;Martin L. Dunn;Yiping Liu;Dudley Finch;Mark Lake;Naseem A. Munshi .Shape memory polymer nanocomposites[J].Acta materialia,2002(20):5115-5126. |
| [4] | 朱光明.形状记忆聚合物的发展及应用[J].工程塑料应用,2002(08):61-63. |
| [5] | 朱光明.新型功能高分子材料--形状记忆聚合物[J].中国科技成果,2003(03):28-31. |
| [6] | Yiping Liu;Ken Gall;Martin L. Dunn;Patrick McCluskey .Thermomechanics of shape memory polymer nanocomposites[J].Mechanics of materials,2004(10):929-940. |
| [7] | 高军鹏,张晨乾,安学锋,张明,益小苏,党国栋,陈春海.含氟聚醚醚酮改性环氧树脂的形状记忆性质研究[C].SAMPE CHINA 2009暨中国国际先进材料与工艺技术学术研讨会论文集,2009:123-126. |
| [8] | Andras Lendlein;Steffen Kelch .Shape-Memory Polymers[J].Angewandte Chemie International Edition,2002(12):2034-2057. |
| [9] | 何曼君;陈维孝;董西侠.高分子物理[M].上海:复旦大学出版社,2005 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%