利用材料试验机开展了室温拉伸实验,在0.001,0.1,0.6s-1不同应变率下,研究了Mg3Al1Zn2Y,Mg3Al2Zn2Y与Mg3Al6Zn2Y合金流动应力的应变率敏感性,其大小为Mg3Al2Zn2Y＞ Mg3Al1Zn2Y＞ Mg3Al6Zn2Y.基于分形理论和计算机图像处理技术,结合扫描电镜分析,研究了合金断裂特征,结果表明:合金在不同应变率拉伸下的断口分形行为显著,分形维数可将断口的韧脆性与形貌特征联系起来,分形维数越大,合金塑性相对越好,合金越倾向于延性断裂,断口形貌也越复杂；三种合金断裂特性的应变率敏感性大小为Mg3Al2Zn2Y＞ Mg3Al6Zn2Y＞Mg3Al1Zn2Y,且表现出正负不同的应变率效应.
参考文献
| [1] | T. Yokoyama .Impact tensile stress-strain characteristics of wrought magnesium alloys[J].Strain,2003(4):167-175. |
| [2] | E. El-Magd;M. Abouridouane .Characterization, modelling and simulation of deformation and fracture behaviour of the light-weight wrought alloys under high strain rate loading[J].International journal of impact engineering,2006(5):741-758. |
| [3] | MEYERS;MARC A.Dynamic Behavior of Materials[M].Beilin:Springer-Verlag,1994:296-302. |
| [4] | ABBOTT T;EASTON MA;SCHMIDT R .Magnesium Technology 2003[R].Tokyo:Magnesium Technology Forum,2003. |
| [5] | Wei Qian Song;Peter Beggs;Mark Easton .Compressive Strain-rate Sensitivity Of Magnesium-aluminum Die Casting Alloys[J].Materials & design,2009(3):642-648. |
| [6] | AUNE TK;ALBRIGHT D;WESTENGEN H .Behavior of die cast magnesium alloys subject to rapid deformation[J].SAE Transactions,2000,109(05):555-559. |
| [7] | 王小强,李全安,张兴渊.Y对AZ81镁合金组织和力学性能的影响[J].特种铸造及有色合金,2007(05):384-387. |
| [8] | 刘方政,许春香,刘彦海,吕正玲.Y对AZ61镁合金金相组织和力学性能的影响[J].铸造设备研究,2008(01):15-17. |
| [9] | 张金旺,许并社.Y对AZ31镁合金铸态组织和性能的影响[J].中北大学学报(自然科学版),2009(02):192-196. |
| [10] | 麻彦龙,左汝林,汤爱涛,张静,潘复生.钇对铸态ZK60镁合金晶界析出相形态的影响[J].重庆大学学报（自然科学版）,2005(02):51-54. |
| [11] | 褚武扬.材料科学中的分形[M].北京:化学工业出版社,2004 |
| [12] | Y.H. Wei;Q.D. Wang;Y.P. Zhu .Superplasticity and grain boundary sliding in rolled AZ91 magnesium alloy at high strain rates[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):107-115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%