采用热压烧结技术制备了Al2O3/Cr3C2/(W,Ti)C复合陶瓷材料,对其物理力学性能、摩擦磨损性能进行测试,用扫描电镜(SEM)对其磨损表面进行观察.结果表明:Al2O3/Cr3C2/(W,Ti)C陶瓷材料具有良好的综合力学性能,在与硬质合金YG8圆环的对磨中表现出较高的减摩抗磨性能,摩擦因子与磨损率较单相Al2O3降低近50％.对其磨损机理研究认为,磨粒磨损为主要磨损机制,高的强度和韧性是其具有良好耐磨性能的主要原因.
参考文献
| [1] | Fu CT.;Li AK. .THE TOUGHENING BEHAVIOURS OF CR3C2 PARTICULATE-REINFORCED AL2O3 COMPOSITES[J].Journal of Materials Science,1996(17):4697-4704. |
| [2] | DENG JIANXIN;DING ZELIANG;ZHAO JUN .Unlubricated friction and wear behaviors of various alumina-based ceramic composites against cemented carbide[J].CERAMICS INTERNATIONAL,2006(5):499-507. |
| [3] | XU C H .Preparation and performance of an advanced multiphase composite ceramic material[J].Journal of the European Ceramic Society,2005,25(05):605-611. |
| [4] | HUANG J L;LIN H D;JENG C A et al.Crack growth resistance of Cr3C2/ Al2O3 composites[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2000,279(1-2):81-86. |
| [5] | LII D F;HUANG J L;TWU K C et al.Investigation of Al2O3/Cr3C2 composites prepared by pressureless sintering(partl)[J].Journal of the Ceramic Society of Japan,1996,104(09):796-801. |
| [6] | 孙德明,鹿晓阳,李成美,薛仲舜,陈怀明,岳雪涛,孙胜.Cr3C2及（W,Ti）C对Al2O3/Cr3 C2/（W,Ti）C复合陶瓷材料Vickers硬度的影响[J].材料工程,2005(11):16-18. |
| [7] | 孙德明,刘立红,鹿晓阳,许崇海,张勤河,艾兴.Al2O3/Cr3C2/（W,Ti）C陶瓷材料的力学性能及微观结构[J].硅酸盐学报,2005(04):411-415. |
| [8] | 孙德明,张勤河,柴琦,张明勤,许崇海.Al2O3/Cr3C2/（W,Ti）C复合材料化学相容性分析[J].材料工程,2007(09):55-57,61. |
| [9] | ERDEMIR A;FENSKE G R .Solid lubrication of ceramic surfaces by LAD-silver coatings for heat engine application[J].Tribology Transactions,1990,33:511-518. |
| [10] | EVANS A G;WILSHAW T R .Quasi-static solid particle damage in brittle solids Ⅰ:Observations,analysis and implications[J].Acta Metallurgica,1976,24:939-956. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%