合成了海因环氧树脂,采用红外光谱和核磁共振进行了表征,以六氢苯酐(HHPA)为固化剂,制备了海因环氧树脂/HHPA体系,研究了海因环氧树脂/HHPA体系的固化反应性及其固化物的性能.结果表明:树脂体系在升温速率为10℃/min的条件下,在90～210℃有一放热峰,峰值温度为152.5℃;100℃下的凝胶时间大于42min,在140℃下为8min;树脂浇铸体的氧指数为23,抗弯强度为122MPa,弯曲模量为2.7GPa,冲击强度为14.9kJ/m2.
参考文献
| [1] | Mercado LA;Galia M;Reina JA .Silicon-containing flame retardant epoxy resins: Synthesis, characterization and properties[J].Polymer Degradation and Stability,2006(11):2588-2594. |
| [2] | Wang WJ.;Hsiue GH.;Chang FC.;Perng LH. .Characterization and properties of new silicone-containing epoxy resin[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(16):6113-6122. |
| [3] | 钱立军;支俊格;佟斌.含磷环氧树脂的合成及改性研究[J].阻燃材料与技术,2007(01):5-9. |
| [4] | Kumar SA;Denchev Z;Alagar M .Synthesis and thermal characterization of phosphorus containing siliconized epoxy resins[J].European Polymer Journal,2006(10):2419-2429. |
| [5] | Hergenrother PM;Thompson CM;Smith JG;Connell JW;Hinkley JA;Lyon RE;Moulton R .Flame retardant aircraft epoxy resins containing phosphorus[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(14):5012-5024. |
| [6] | LIU Ran;WANG Xiao-dong .Synthesis,characterization,thermal properties and flame retardancy of a novel nonflamable phosphazene-based epoxy resin[J].Polymer Degradation and Stability,2009,94:617-624. |
| [7] | 徐伟箭,周晓,夏新年.新型含氮阻燃环氧树脂的合成与性能[J].湖南大学学报（自然科学版）,2006(04):72-75. |
| [8] | 熊涛,王锦艳,兰建武,于艳,蹇锡高.含二氮杂萘酮结构新型环氧树脂的合成[J].石油化工,2003(05):426-429. |
| [9] | 万红梅,张兴宏,闵玉勤,方佐,戚国荣.一种新型含氮环氧树脂的合成[J].浙江大学学报(理学版),2004(06):646-651. |
| [10] | 马承银 .水溶性海因环氧树脂合成方法[P].中国专利:101307131A,2008-11-19. |
| [11] | 段华军,王钧,杨小利.低粘度环氧树脂固化体系研究[J].玻璃钢/复合材料,2003(01):32-34. |
| [12] | 夏建陵,蒋澄,王定选.桐酐与甲基四氢苯酐复合固化环氧体系的性能[J].热固性树脂,2006(04):5-8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%