多孔硅吸杂是减少晶体硅中杂质和缺陷,提高太阳能电池转换效率的有效方法.采用电化学腐蚀方法在单晶硅片上制备多孔硅,通过观察多孔硅的形貌、结构及单晶硅片的电阻率变化,研究不同电流密度制备的多孔硅对吸杂效果的影响,并从多孔硅的结构出发探究多孔硅吸杂的机理.结果表明,随电流密度增加,孔隙率明显增加,多孔硅在电流密度为100mA/cm2时,孔隙率最大;电流密度越大,多孔硅伴随所产生的弹性机械应力增加,晶格常数相应增加,这两个因素都有利于缺陷和金属杂质在多孔硅层-基底界面处迁移和富集,导致单晶硅吸杂后电阻率增大.
参考文献
| [1] | 王书荣,陈庭金,刘祖明,魏晋云,胡志华,廖华,李迎军.多晶硅太阳电池的吸杂实验研究[J].云南师范大学学报(自然科学版),2001(06):43-44. |
| [2] | 杨德仁.硅材料的吸杂研究[J].半导体技术,1992(08):53-56. |
| [3] | 汤艳 .直拉单晶硅内吸杂研究[D].浙江大学,2002. |
| [4] | JOOSS W;HAHN G;FATH P.Improvement of diffusion lengths in multicrystalline silicon by P/A1 co-gettering during solar cell processing[A].Vienna,Austria,1998:689-695. |
| [5] | Spiecker E.;Schroter W.;Seibt M. .PHOSPHOROUS-DIFFUSION GETTERING IN THE PRESENCE OF A NONEQUILIBRIUM CONCENTRATION OF SILICON INTERSTITIALS - A QUANTITATIVE MODEL[J].Physical Review.B.Condensed Matter,1997(15):9577-9583. |
| [6] | JOSHI S M;GOSELE U M;TAN T Y .Improvement of minority carrier diffusion length in silicon by aluminum gettering[J].Applied Physics Letters,1995,77(08):3858-3863. |
| [7] | GAY-HENQUINET N;MARTINUZZI S.Efficiency of nanocavity backside gettering in multicrystalline silicon wafers[A].Vienna,Austria,1998:1599-1602. |
| [8] | Khedher N.;Hajji M.;Bouaicha M.;Boujmil MF.;Ezzaouia H.;Bessais B. Bennaceur R. .Improvement of transport parameters in solar grade monocrystalline silicon by application of a sacrificial porous silicon layer[J].Solid State Communications,2002(1/2):7-10. |
| [9] | Khedher N;Ben Jaballah A;Hassen M;Hajji M;Ezzaouia H;Bessais B;Selmi A;Bennaceur R .Gettering by heat thermal processing: application in crystalline silicon solar cells[J].Materials science in semiconductor processing,2004(4/6):439-442. |
| [10] | Hassen M;Ben Jaballah A;Hajji M;Khedher N;Bessais B;Ezzaouia H;Rahmouni H;Ouaja FR;Selmi A .Performance improvements of crystalline silicon by iterative gettering process for short duration and with the use of porous silicon as sacrificial layer[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2005(1/4):493-499. |
| [11] | LIN C S;FANG S K .Formation of cerium conversion coatings on AZ31 magnesium alloys[J].Electrochemical Society,2005,152(02):B54. |
| [12] | 谢荣国,席珍强,马向阳,袁俊,杨德仁.用化学腐蚀制备多孔硅太阳电池减反射膜的研究[J].材料科学与工程,2002(04):507-509,567. |
| [13] | Strehlke S.;Levy-Clement C.;Bastide S. .Optimization of porous silicon reflectance for silicon photovoltaic cells[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,1999(4):399-409. |
| [14] | SMITH R L;COLLINGS S D .Porous silicon formation mechanisms[J].Applied Physics,1992,71(08):R1-R22. |
| [15] | 张树霖.多孔硅--一种新形态的硅材料[J].物理,1992(08):478. |
| [16] | YOUNG I M;BEALE M I J;BENJAMIN J D .X-ray double crystal diffraction study of Porous silicon[J].Applied Physics Letters,1985,46(12):1133-1135. |
| [17] | Bilyalov R.;Beaucarne G.;Loo R.;Caymax M.;Poortmans J. Nijs J.;Stalmans L. .Porous silicon as an intermediate layer for thin-film solar cell[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2001(1/4):477-485. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%