利用电火花沉积技术,采用自制电极在P20钢基材表面沉积Ni-Cr合金涂层,研究了沉积层的组织特征、显微硬度分布及耐磨、耐蚀性能.结果表明:通过优化沉积工艺参数可以获得厚度高达430μm的沉积层.电火花沉积层与基体的结合界面属于非均匀混合互熔结晶型界面,沉积层与基体呈现良好的冶金结合;涂层中下部组织为细小的枝晶组织,而上部组织为纳米晶结构.沉积层的硬度呈梯度分布,涂层外层硬度值最高.涂层的耐磨、耐蚀性能比基体有较大提高,涂层上部超细的纳米晶结构是其耐磨性能及耐蚀性能提高的主要因素.
参考文献
| [1] | Zamulaeva EI;Levashov EA;Kudryashov AE;Vakaev PV;Petrzhik MI .Electrospark coatings deposited onto an Armco iron substrate with nano- and microstructured WC-Co electrodes: Deposition process, structure, and properties[J].Surface & Coatings Technology,2008(15):3715-3722. |
| [2] | Ribalko AV.;Sahin O. .The use of bipolar current pulses in electrospark alloying of metal surfaces[J].Surface & Coatings Technology,2003(2/3):129-135. |
| [3] | 罗成,董仕节,熊翔,罗平.Cr12MoV钢表面电火花沉积TiB2涂层特性研究[J].模具工业,2009(03):63-67. |
| [4] | 张富巨,华爱兵,徐锴,马立卿.填充型电火花精密堆焊接头的界面结合行为[J].焊接学报,2004(03):113-116. |
| [5] | Levashov EA;Vakaev PV;Zamulaeva EI;Kudryashov AE;Kurbatkina VV;Shtansky DV;Voevodin AA;Sanz A .Disperse-strengthening by nanoparticles advanced tribological coatings and electrode materials for their deposition[J].Surface & Coatings Technology,2007(13):6176-6181. |
| [6] | 罗成,熊翔,董仕节,罗平.点焊电极表面电火花沉积TiB_2涂层的特征[J].材料热处理学报,2009(06):178-182. |
| [7] | 罗成,董仕节,熊翔.电火花振动沉积TiC功能涂层的显微组织与性能[J].材料热处理学报,2008(02):123-127. |
| [8] | Frangini S.;Masci A.;Di Bartolomeo A. .Cr7C3-based cermet coating deposited on stainless steel by electrospark process: structural characteristics and corrosion behavior[J].Surface & Coatings Technology,2002(2/3):279-286. |
| [9] | 毕晓勤,杨仲磊,胡小丽.等离子熔覆Ni-Cr合金涂层的组织与性能研究[J].材料工程,2009(05):26-29. |
| [10] | 黄俊,吴红艳,毕强,张平则,姜云东.双辉等离子表面Ni-Cr合金渗层的组织及耐蚀性能研究[J].材料工程,2010(11):79-82. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%