采用二步阳极氧化法制备孔结构高度有序的多孔氧化铝(AAO)模板.在不同Fe2+/Co2+摩尔比的电解液中,利用交流电化学沉积,在模板孔内成功制备了FeCo合金纳米线阵列.分别采用透射电子显微镜(TEM),场发射扫描电子显微镜(FE-SEM),X射线衍射仪(XRD)和震动样品磁强计(VSM)对样品的形貌,结构及磁学性能进行了表征.结果表明,制备的FeCo合金纳米线排列有序,粗细均匀;其直径与模板孔径一致,填充率较高,且具有明显的[110]择优取向.VSM测试结果表明,不同溶液浓度下制备的FeCo合金纳米线阵列均具有良好的垂直磁各向异性,易磁化轴沿着纳米线轴线方向.随着电解液Fe2+/Co2+摩尔比的不同,可在一定范围内对FeCo合金纳米线阵列的磁性进行调控,并对其原因进行了讨论.
参考文献
| [1] | Shaoguang Yang;Hao Zhu;Dongliang Yu .Preparation and magnetic property of Fe nanowire array[J].Journal of Magnetism and Magnetic Materials,2000(1/2):97-100. |
| [2] | WU Chen-guey;LIN Hu-leng;SHAU Nai-ling .Magnetic nanowires via template electrodepositing[J].Journal of Solid State Electrochemistry,2006,10:198-202. |
| [3] | 姚素薇,迟广俊,崔兰,范君,张卫国,王宏智.模板组装Fe纳米线阵列及其微结构[J].物理化学学报,2002(10):930-933. |
| [4] | H. R. Khan;K. Petrikowski .Synthesis and properties of the arrays of magnetic nanowires of Co and CoFe[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2002(1/2):345-348. |
| [5] | Jinxia Xu;Yi Xu .Fabrication and magnetic property of binary Co-Ni nanowire array by alternating current electrodeposition[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(17):7203-7206. |
| [6] | Yang, W;Cui, CX;Sun, JB;Wang, BL .Fabrication and magnetic properties of Fe3Co7 alloy nanowire arrays[J].Journal of Materials Science,2010(6):1523-1527. |
| [7] | Cao L;Qiu XP;Ding JB;Li HL;Chen LQ .The effects of composition and thermal treatment on the magnetic properties of Fe100-xCox nanowire arrays based on AAO templates[J].Journal of Materials Science,2006(8):2211-2218. |
| [8] | Khan HR.;Petrikowski K. .Magnetic and structural properties of the electrochemically deposited arrays of Co and CoFe nanowires[J].Journal of Magnetism and Magnetic Materials,2002(3):458-461. |
| [9] | 王学华,李承勇,马连娇,刘军,曹宏.高度有序AAO孔的结构参数及其分布规律[J].材料工程,2008(10):219-222,227. |
| [10] | 覃东欢,力虎林.Fe0.3Co0.7纳米有序阵列的制备和磁性[J].材料研究学报,2007(05):501-505. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%