研究激光金属成形DZ125L高温合金的组织,其形成的非平衡组织致密,一次枝晶间距约5μm；生成的过饱和固溶体抑制γ'相析出,且晶界析出点状不连续MC碳化物.这无法满足高温合金直接使用要求,需进行必要热处理.因此研究了5种热处理状态下的组织和显微硬度,结果表明均匀化和固溶处理十分必要,但需严格控制时间；时效处理时间可以适当减少.经过热处理试样的硬度比未经过过热处理试样硬度低,主要原因是激光金属成形组织细密,晶界析出大量强化相MC碳化物.
参考文献
| [1] | A.J. Elliott;S. Tin;W.T. King .Directional Solidification of Large Superalloy Castings with Radiation and Liquid-Metal Cooling: A Comparative Assessment[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2004(10):3221-3231. |
| [2] | Jian ZHANG,Langhong LOU.Directional Solidification Assisted by Liquid Metal Cooling[J].材料科学技术学报（英文版）,2007(03):289-300. |
| [3] | FU H Z;GENG X .High rate directional solidification and its application in single crystal superalloys[J].Science and Technology of Advanced Materials,2001,2(01):197-204. |
| [4] | LIU L;HUANG T W;ZHANG J et al.Microstructure and stress rupture properties of single crystal superalloy CMSX-2 under high thermal gradient directional solidification[J].Materials Letters,2007,61(01):227-230. |
| [5] | 张亚玮,张述泉,王华明.激光熔化沉积定向快速凝固高温合金组织及性能[J].稀有金属材料与工程,2008(01):169-172. |
| [6] | 闵志先,沈军,王灵水,冯周荣,刘林,傅恒志.定向凝固镍基高温合金DZ125平界面生长的微观组织演化[J].金属学报,2010(09):1075-1080. |
| [7] | 陈荣章,佘力,张宏炜,王罗宝.DZ125定向凝固高温合金的研究[J].航空材料学报,2000(04):14-19. |
| [8] | 张安峰;李涤尘;卢秉恒 .激光直接金属快速成形技术的研究进展[J].兵器材料科学与工程,2000,20(04):14-19. |
| [9] | Lino Costa;Rui Vilar .Laser powder deposition[J].Rapid prototyping journal,2009(4):264-279. |
| [10] | 黄卫东;林鑫;陈静.激光立体成形[M].西安:西北工业大学出版社,2007:1-20. |
| [11] | HUNT J D.In Solidification and Casting of Metals[M].London:The Metal Society,1979 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%