通过对Ti-35V-15Cr-0.15Si-0.05C合金轧制环件取样进行热处理和热稳定性能实验,研究了850℃和950℃固溶处理和950℃固溶后在600℃和700℃实效后的热稳定性能和微观组织.结果表明:合金仅经过固溶处理α相析出不明显,而经过固溶加时效处理后α相在晶界和晶内大量析出,在热稳定性能测试时,经过540℃100h热暴露后,α相进一步析出.合金α相是影响合金拉伸性能的主要因素,在晶界析出的连续α相导致合金塑性急剧下降；通过850℃固溶热处理能够获得较好的室温拉伸和热稳定性能.
参考文献
| [1] | BOYER R R .An overview on the use of titanium in the aerospace industry[J].Materials Science and Engineering A,1996,213:103-114. |
| [2] | LI Y G;BLENKINSOP P A;LORETTO M H et al.Effect of carbon and oxygen on microstructure and mechanical properties of Ti-25V-15Cr-Al alloy[J].Acta Materials,1999,47(10):2889-2892. |
| [3] | 雷力明,黄旭,孙福生,D.Rugg,W.Voice,曹春晓.碳化物分布状态对Ti-25V-15Cr-2Al-0.2C-x合金微观组织的影响[J].稀有金属材料与工程,2004(06):632-634. |
| [4] | Phase Diagram of Binary Titanium Alloys[S].ASM International,Materials Park,1987. |
| [5] | LI Y G;LORETTO M H;RUGG D et al.Effect of heat treatment and exposure on microstructure and mechanical properties of Ti-25V-15Cr-2Al-0.2C alloy[J].Acta Materials,2001,49:3011-3015. |
| [6] | 雷力明 .低成本β稳定型阻燃钛合金的微观组织和力学性能研究[D].北京:北京航空材料研究院,2001. |
| [7] | HANDA S;IZUMI O .Correlation of stability in commercial β-phase titanium alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1987,18(02):265-271. |
| [8] | 赵永庆,曲恒磊,朱康英,吴欢,刘彩利,周廉.β型Ti40阻燃钛合金高温长期作用的第二相及其对性能的影响[J].稀有金属材料与工程,2002(02):84-88. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%