采用Thermo-calc热力学计算软件以及JMatPro分析软件对DD6镍基单晶高温合金真空感应熔炼过程中氧化物夹杂形成的热力学条件进行了计算分析.结果表明:DD6单晶高温合金熔化和凝固过程中形成的氧化物夹杂主要为Al2O3.热力学平衡状态下,熔化阶段和凝固阶段合金液中氧的活度分别在(3.21～14.0)×10-7,(1.63～4.89)×10-8 范围内.在真空度为0.1Pa时,采用CaO坩埚熔炼DD6合金将会造成熔体增氧和Al2O3夹杂的产生.为了使Al2O3夹杂含量降低至10×10-6以下,合金化开始前应将氧的含量控制在4.709×10-6以内.
参考文献
| [1] | COCKCROFT S L;DEGAWA T;MITCHELL A.Inclusion precipitation in superalloy[A].Champoin,Pennsylvania:TMS,1992:577-586. |
| [2] | MITCHELL A.Progress in understanding clean metal production for IN718[A].Pittsburgh,Pennsylvania:TMS,1994:109-123. |
| [3] | SIDDALL R J.Comparison of the attributes of VIM + ESR and VIM+VAR Alloy718[A].Pittsburgh,Pennsylvania:TMS,1991:29-40. |
| [4] | J. P. Niu;X. F. Sun;T. Jin .Investigation into deoxidation during vacuum induction melting refining of nickel base superalloy using CaO crucible[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(4):435-439. |
| [5] | 陈荣章.单晶高温合金发展现状[J].材料工程,1995(08):3. |
| [6] | X. J. Liu;K. Oikawa;I. Ohnuma .The Use of Phase Diagrams and Thermodynamic Databases for Electronic Materials[J].JOM,2003(12):53-59. |
| [7] | N. Saunders;Z. Guo;X. Li .Using JMatPro to Model Materials Properties and Behavior[J].JOM,2003(12):60-65. |
| [8] | Saunders N;Miodownik AP;Schille JP .Modelling of the thermo-physical and physical properties for solidification of Ni-based superalloys[J].Journal of Materials Science,2004(24):7237-7243. |
| [9] | SAUNDERS N.Phase diagram calculations for Ni-based superalloys[A].Champion,Pennsylvania:TMS,1996:101-110. |
| [10] | 曲英;项长祥;姜钧普 等.冶金熔体中组元活度及其标准态的量[J].上海大学学报,2005,5(11):546-549. |
| [11] | 牛建平.纯净钢及高温合金制备技术[M].北京:冶金工业出版社,2009 |
| [12] | 魏寿昆.冶金过程热力学[M].北京:科学出版社,2010 |
| [13] | 丁永昌.特种熔炼[M].北京:冶金工业出版社,1995 |
| [14] | 牛建平,杨克努,孙晓峰,金涛,管恒荣,胡壮麒.用CaO坩埚真空感应熔炼镍基高温合金脱氧研究[J].金属学报,2002(03):303-308. |
| [15] | 傅恒志;郭景杰;刘林.先进材料定向凝固[M].北京:科学出版社,2008 |
| [16] | 吴仲棠.DD3单晶合金的真空感应熔炼[J].材料工程,1995(06):35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%