在第三代Ni基单晶高温合金上制备NiCoCrAlYHf(HY5)高温抗氧化涂层,采用扫描电镜(SEM),能谱分析(EDS)和X射线衍射(XRD)等手段,对涂层表面及界面进行组织形貌观察和相结构分析,研究涂层试样的循环氧化动力学和元素互扩散行为.结果表明:采用真空电弧镀(AIP)方法制备的HY5涂层,提高了单晶高温合金的循环抗氧化能力;在1100℃大气环境中扩散600h后,涂覆HY5涂层的单晶高温合金基体中形成了互扩散区IDZ,互扩散主要由Cr,Ni元素从基体向高温抗氧化涂层的外扩散以及Al元素从高温抗氧化涂层向基体的内扩散构成;在涂层下方60μm左右有拓扑密堆相TCP析出,并形成二次反应区SRZ.
参考文献
| [1] | 牟仁德,陆峰,何利民,贺世美,黄光宏.热障涂层技术在航空发动机上的应用与发展[J].热喷涂技术,2009(01):53-58,66. |
| [2] | 黄光宏,王宁,何利民,牟仁德,贺世美.环境障涂层研究进展[J].失效分析与预防,2007(01):59-64. |
| [3] | 牟仁德,贺世美,何利民,许振华.微叠层结构EB-PVD热障涂层[J].航空材料学报,2009(03):55-60. |
| [4] | D. F. SUSAN;A. R. MARDER .Ni-Al COMPOSITE COATINGS: DIFFUSION ANALYSIS AND COATING LIFETIME ESTIMATION[J].Acta materialia,2001(7):1153-1163. |
| [5] | 潘金生;田民波.材料科学基础[M].北京:清华大学出版社,1998 |
| [6] | 徐滨士.表面工程与维修[M].北京:机械工业出版社,1996:85-87. |
| [7] | 徐惠彬,宫声凯,刘福顺.航空发动机热障涂层材料体系的研究[J].航空学报,2000(01):7-12. |
| [8] | KARUNARTNEMSA;RAECM F;REEDRC .On the microstructural instability of an experimental nickel base single crystal superalloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2001,32(10):24092421. |
| [9] | C. M. F. RAE;R. C. REED .THE PRECIPITATION OF TOPOLOGICALLY CLOSE-PACKED PHASES IN RHENIUM-CONTAINING SUPERALLOYS[J].Acta materialia,2001(19):4113-4125. |
| [10] | 熊玉明,李明升,李松林.热障涂层与镍基高温合金界面的互扩散行为[J].粉末冶金材料科学与工程,2007(02):63-69. |
| [11] | 田贺,牟仁德,何利民,李建平.粘结层成分对单晶合金热障涂层寿命影响研究[J].失效分析与预防,2012(04):228-234. |
| [12] | CHEN Xiao-qun .Progressive damage and failure of thermal barrier coatings[D].Detroit:Wayne State University,2001. |
| [13] | Muller J.;Neuschutz D. .Efficiency of alpha-alumina as diffusion barrier between bond coat and bulk material of gas turbine blades[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2003(1/2):247-251. |
| [14] | STOTT F H;SHIDA Y;WHITTLE D P et al.Development of preferential integranular oxides in nickel-aluminum alloys at high temperatures[J].Oxidation of Metals,1982,18(03):127-135. |
| [15] | 陈和兴 .镍基合金基体热障涂层界面扩散和反应的研究[D].中南大学,2004. |
| [16] | CZECH N;SCHMITZ F;SRAMM W .Microstructural analysis of the role of rhenium in a advanced MCrAlY coatings[J].Surface and Coatings Technology,1995,76-77(01):28-33. |
| [17] | Beele W;Czech N;Quadakkers WJ;Stamm W;Siemens AG Power Generat D-45466 Mulheim Germany. .Long-term oxidation tests on a Re-containing MCrAlY coating[J].Surface & Coatings Technology,1997(1/3):41-45. |
| [18] | NARITA T;YOSHIDA D .Heat-resistant nickel alloy composite excellent in high temperature oxidation resistance[P].USA Patent:7285337,2007-10-23. |
| [19] | C.Z. Xu;S.M. Jiang;Z.B. Bao;J. Gong;C. Sun .Isothermal oxidation behaviour of a gradient NiCoCrAlSiY coating deposited by arc ion plating on a Ni-based single crystal superalloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(6):1467-1474. |
| [20] | J.D.Nystrom .Discontinuous Cellular Precipitation in a High-Refractory Nickel-Base Superalloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1997(12):2443-2452. |
| [21] | Suzuki, A.S.;Kawagishi, K.;Yokokawa, T.;Harada, H. .Effect of Cr on microstructural evolution of aluminized fourth generation Ni-base single crystal superalloys[J].Surface & Coatings Technology,2012(11/12):2769-2773. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%