将不同冷轧压下率的低碳铝镇静钢进行不同保温温度和时间的退火再结晶实验研究,利用维氏硬度计、金相显微镜和X射线衍射仪研究了退火后试样的硬度、金相显微组织及织构的变化情况.结果表明:在相同的退火工艺制度条件下,随着冷轧压下率的增加,再结晶开始和结束温度降低,晶粒尺寸减小.当冷轧压下率升高到68%后,冷轧压下率的增加对再结晶晶粒细化的作用减弱,甚至没有细化作用;680℃保温退火时,一开始就发生了再结晶,基本不需要孕育期.随着保温时间的延长,晶粒均匀长大,晶粒饼形程度增加;退火温度由660℃升高到720℃时,{111}面有利织构增加,{100}面不利织构减少,720℃退火温度较为适宜.冷轧压下率为58%的试样在760℃退火时发生了二次再结晶对实验钢板的力学性能产生不利影响.

参考文献

[1] TAKECHI H .Metallurgy aspects on IF steel from industrial viewpoint[J].ISIJ International,1994,34(01):3-7.
[2] Yuhua Song;Yongnian Yan;Renji Zhang .Manufacture of the die of an automobile deck part based on rapid prototyping and rapid tooling technology[J].Journal of Materials Processing Technology,2002(1/3):237-242.
[3] 胡卓超,蒋奇武,赵骧,左良.预回复对08Al深冲钢板再结晶组织及织构的影响[J].东北大学学报(自然科学版),2001(02):146-149.
[4] Von SCHLIPPENBACH U;EMREN F;LUCKE K .Investiga tion of the development of the cold rolling texture in deep drawing steels by ODF-analysis[J].ACTA METALLURGICA,1986,34(07):12891301.
[5] 康永林.现代汽车板的质量控制与成形性[M].北京:冶金工业出版社,1999
[6] 赵新兵;LUKE K .计算晶粒尺寸分布的几何模型及实用方法[J].金属学报,1992,28(08):343-350.
[7] A. Martinez-de-Guerenu;F. Arizti;M. Diaz-Fuentes .Recovery during annealing in a cold rolled low carbon steel. Part I: Kinetics and microstructural characterization[J].Acta materialia,2004(12):3657-3664.
[8] 毛卫民.金属材料的晶体学织构与各向异性[M].北京:科学出版社,2002:812.
[9] V.J. Martinez;J.I. Verdeja;J.A. Pero-Sanz .Interstitial free steel Influence of #alpha#-phase hot-rolling and cold-rolling reduction to obtain extra-deep drawing quality[J].Materials Characterization,2001(1):45-53.
[10] WANG R Z;LEI T C .Dynamic recrystallization of ferrite in a low carbon steel during hot rolling in the (F+A) two-phase range[J].Scr MetallMater,1994,31(09):1193-1196.
[11] WANG R Z;LEI T C .Substructural evolution of ferrite in a low carbon steel during hot deformation in (F+A) two phase range[J].ScrMetallMater,1993,28(05):629-632.
[12] BELYAKOV A;KAIBYSHEV R;ZARIPOVA R .High-tem perature mechanism of dynamic recrystallization of ferrite steel[J].MaterSciForum,1993,113-115(05):385-390.
[13] GAO F;SONG B Y;XU Y R et al.Substructural changes during hot deformation of an Fe-26Cr ferritic stainless steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31(01):21-27.
[14] Hiroyuki Yagi;Nobuhiro Tsuji;Yoshihiro Saito .Dynamic recrystallization in 18%Cr ferritic steel[J].鉄と鋼,2000(5):349-356.
[15] N. Tsuji;Y. Matsubara;Y. Saito .Dynamic recrystallization of ferrite in interstitial free steel[J].Scripta materialia,1997(4):477-484.
[16] 刘浩,陈晓,吴润,余晓静,彭涛.再结晶退火对含磷冷轧高强度钢板显微组织的影响[J].武汉科技大学学报(自然科学版),2006(05):449-451.
[17] Xiang ZHAO,Zhuochao HU,Liang ZUO.Effects of External Electric Field on AlN Precipitation and Recrystallization Texture of Deep-drawing 08Al Killed Steel Sheet[J].材料科学技术学报(英文版),2006(06):747-750.
[18] RAY R K;JONAS J J .Transformation textures in steels[J].Int Met Rev,1990,35(06):1-36.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%