将AZ10,AZ31,AZ61,AZ91镁合金在Gleeble1500D热模拟试验机上进行热模拟挤压实验,并对挤压制品的组织均匀性及其影响因素进行分析.结果表明:合金含量、均匀化预处理与否及挤压比是挤压制品组织均匀性最重要的影响因素.挤压前经均匀化预处理比未经均匀化预处理的镁合金挤压组织更均匀,但晶粒更大,并且未经均匀化预处理的镁合金挤压组织具有未发生再结晶的岛状组织.合金元素含量越高的镁合金挤压组织越不均匀,但晶粒越细小.随着挤压比的增大,组织趋于均匀.
参考文献
| [1] | Manfred Geiger;Marion Merklein .Sheet metal forming - a new kind of forge for the future?[J].Key engineering materials,2007(344):9-20. |
| [2] | S. Schumann .The Paths and Strategies for Increased Magnesium Applications In Vehicles[J].Materials Science Forum,2005(0):1-8. |
| [3] | G. Palumbo;D. Sorgente;L. Tricarico .Numerical-experimental analysis of thin magnesium alloy stripes subjected to stretch-bending[J].Journal of Materials Processing Technology,2008(1-3):183-188. |
| [4] | M.El Mehtedi;L.Balloni;S.Spigarelli;E.Evangelista;G.Rosen .Hot Workability and Constitutive Equations of ZM21 Magnesium alloy[J].Key engineering materials,2008(0):79-86. |
| [5] | SWIOSTEK J;LETZING D;KAINER K U .Hydrostatic extrusion at 100℃ and its effect on the grain size and mechanical properties of magnesium alloys[J].METAL SCIENCE AND HEAT TREATMENT,2006,48(11-12):499-503. |
| [6] | DALE L. ATWELL;MATTHEW R. BARNETT .Extrusion Limits of Magnesium Alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2007(12):3032-3041. |
| [7] | 黎文献.镁及镁合金[M].长沙:中南大学出版社,2005 |
| [8] | 曾小勤,丁文江,姚正裔,彭立明,卢晨.Mg-Zn-Al系合金组织和力学性能[J].上海交通大学学报,2005(01):46-51. |
| [9] | 宋成猛,彭建,刘天模.AZ10镁合金均匀化退火工艺研究[J].材料导报,2007(z2):382-384. |
| [10] | 谢建新;刘静安.金属挤压理论与技术[M].北京:冶金工业出版社,2001:1-7. |
| [11] | 彭建,王中国,刘虹,宋成猛.退火工艺对 AZ61镁合金铸坯组织及加工性能的影响[J].材料导报,2007(z2):378-379,384. |
| [12] | 钟皓,陈琪,闫蕴琪,张慧,翁文凭.AZ31镁合金的热挤压组织与力学性能分析[J].轻金属,2007(03):52-55. |
| [13] | 徐春杰,张忠明,郭学锋,贾树卓,刘礼,孟令楠.热挤压AZ91D镁合金的组织与力学性能[J].西安理工大学学报,2005(04):356-360. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%