使用Gleeble 3800试验机对铸态Inconel 625合金进行了一系列条件的热压缩实验,根据动态材料模型建立了热加工图,并结合真应力-真应变曲线及微观组织,分析了合金在不同条件下的变形机制.结果表明:对铸态625合金,1273～1363K,0.1～5.05s1为动态回复区;1363～1453K,0.1～5.05s-1为不充分动态再结晶区;1400～1453K,5.05～10s1为完全动态再结晶区.该合金在0.1～10s 1变形时,发生动态再结晶的临界温度在1373～1423K之间,临界应变在0.4～0.6之间.Inconel 625合金不发生失稳流变的条件范围为1400～1453K,5.05～10s-1.
参考文献
| [1] | CIES1AK M J;HEADLEY T J .A melting and solidification study of alloy 625[J].METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,1988,19(09):2319-2331. |
| [2] | M.D. Mathew;P. Parameswaran;K. Bhanu Sankara Rao .Microstructural changes in alloy 625 during high temperature creep[J].Materials Characterization,2008(5):508-513. |
| [3] | PRASAD Y V R K;GEGEL H L;DORAIVELU S M et al.Modeling of dynamic material behavior in hot deformation:forging of Ti 6242[J].METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,1984,15(10):1883-1892. |
| [4] | Murty SVS.;Rao BN. .Ziegler's criterion on the instability regions in processing maps[J].Journal of Materials Science Letters,1998(14):1203-1205. |
| [5] | Prasad YVRK.;Seshacharyulu T. .Processing maps for hot working of titanium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):82-88. |
| [6] | O. Sivakesavam;Y.V.R.K. Prasad .Hot deformation behaviour of as-cast Mg-2Zn-1Mn alloy in compression: a study with processing map[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):118-124. |
| [7] | S.V.S. Narayana Murty;B. Nageswara Rao;B.P. Kashyap .Identification of flow instabilities in the processing maps of AISI 304 stainless steel[J].Journal of Materials Processing Technology,2005(2):268-278. |
| [8] | PRASAD Y V R K .Recent advances in the science of mechanical processing[J].IndianJ Tech,1990,28(6 8):435-451. |
| [9] | ZIEGLER H.Progress in Solid Mechanics[M].New York:Wiley Press,1963:4-93. |
| [10] | VENUGOPAL S;MANNAN S L;PRASAD Y V R K .Pro cessing map for cold and hot working of stainless steel type AISI 304L[J].Materials Letters,1992,15(1-2):79-83. |
| [11] | RAVICHANDRAN N;PRASAD Y V R K .Dynamic recrystallization during hot deformation of aluminum:a study using processing maps[J].METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,1991,22(10):2339-2348. |
| [12] | SESHACHARYULU T;MEDEIROS S C;FRAZIER W G et al.Unstable flow during supratransus working of Ti-6A1-4V[J].Materials Letters,2001,47(03):133139. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%