评述Ni-18Al-4Ti合金由于形成γ'基体/γ共格析出颗粒的独特组织结构而在高温蠕变试验中所表现出来的长时间"零蠕变"现象.应用Hirsch等人关于高层错能基体/低层错能共格析出颗粒的强化理论,可以对此现象作出很好解释,并由此指出一种值得重视的有效高温强化机制.对获得这种组织结构所需的化学成分和工艺条件也作了讨论,认为快速凝固工艺是实现这类合金的重要手段之一.
参考文献
| [1] | R G Davies;T L Johnston;B H Kear.Ordered Alloys[M].Baton Rouge,La:Claitor's Pub-lishing Division,1970:447. |
| [2] | R K Ham;R H Cook;G R Purdy;G.Wil-loughby .[J].METAL SCIENCE JOURNAL,1972,6:205. |
| [3] | P B Hirsch;A Kelly .[J].Philosophical Magazine,1965,12:881. |
| [4] | N S Stoloff .[J].International Materials Reviews,1989,34(03):153. |
| [5] | W H Tian;T Sano;M Nemolo .[J].Journal of the Japan Institute of Metals,1990,54:276. |
| [6] | Yijian LIN R W .[J].Cahn Phys stat sol,1992,131:481. |
| [7] | S M Copley;B H Kear .[J].Transactions of the Metallurgical Society of AIME,1967,239:984. |
| [8] | K J Hemker;M Jmills;W D Nix .[J].Acta Materialia,1991,39:1901. |
| [9] | R W Cahn;P A Siemers;E L Hall .[J].Acta Materialia,1987,35(11):2753. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%