经试验测得了IC-218合金(含少量共格γ相的Ni3Al(B)-Cr基合金)的回复激活能和再结晶激活能,得到相同的数值:230kJ/mol.这与显微组织的观察结果相互印证,即IC-218合金的再结晶主要依靠小角晶界的运动,而大角晶界则失去明显可动性.由此进一步证实,IC-218合金特别迟缓的再结晶动力学根源在于大角晶界失去了明显可动性.以此为基础,对文献报道中关于Ni3Al(B)再结晶研究结果的明显分歧作出了解释.
参考文献
| [1] | 林一坚.IC-218合金的特殊再结晶动力学[J].上海金属,2002(03):8-12. |
| [2] | 林一坚,吴杏芳,柯俊.IC-218合金再结晶时的晶界迁移[J].钢铁研究学报,2002(02):44-48. |
| [3] | 林一坚;Robert W Cahn .共格γ/γ界面对位错运动的单向阀门作用[J].钢铁研究学报,1994,6(03):47. |
| [4] | G Gottstein;P Nagpal;W Kim .Recrystallization and texture in boron doped Ni3Al[J].Materials Science and Engineering,1989,108:165. |
| [5] | N P Zulina;E V Bolberova;I M Razumovskii .Nickle self-diffusion along grain boundary in Ni3Al-base intermetalic alloys[J].Acta Materialia,1996,44:3625. |
| [6] | J Zhu;Z Y Cheng;D X Zou .The deformation of degree of order of nearby grain boundary in the Ni3Al[J].Scripta Metallurgica et Materialia,1990,24:439. |
| [7] | J Ball;G Gottstein .Large strain deformation of Ni3Al+B:PartⅡ.Microstructure and texture evolution during recrystallization[J].INTERMETALLICS,1993,1:191. |
| [8] | 林一坚;吴杏芳;柯俊 .IC-218合金再结晶中织构的变化[J].金属学报,1995,31:421. |