研究Ti-C-Al-Ni系热爆合成NiAI/TiC的形貌,并进行了热力学分析.结果表明:Ti、C含量对产物形貌有显著影响.当体系中Ti、C含量较少(≤15%)时,TiC和NiAl均为圆球状.随着Ti、C含量的增加,NiAl发生熔化;当Ti、C含量达50%左右,TiC颗粒镶嵌在熔融的NiAl基体上,形成较致密的金属间化合物基复合材料;Ti、C含量进一步增加,TiC颗粒变得粗大且不规则,少量NiAl覆盖于其上.产物形貌实际上是由燃烧反应的绝热温度Tad和瞬时液相量所决定的.随着TiC含量的增加,反应体系的Tad提高,NiAl液相量增加,当Ti、C含量达50%时,合成产物中液相量达到最大.
参考文献
[1] | Shun Kangning;Yi Yansheng;Li Aimin.Intermetallic compound/ceramic composites[M].北京:机械工业出版社,2003 |
[2] | Noebe RD;M isra A;Gibala .Plastic Flow and fracture of B2 NiAlbased intermetallic alloys containing a ductile second phase[J].ISU International,1991,31(10):1172-1185. |
[3] | Misra A;Gibala R .Room temperature deformation behavior of a directionally solidified B2-(Ni-Fe-Al) intermatallic alloy[J].Metallurgical and Materials Transactions,1997,28A(03):795-807. |
[4] | Huang S C;Field R D;krueger DD .Microscopy and tensile behavior of melt-spun Ni-Al-Fe alloys[J].Metallurgical and Materials Transactions,1990,21A(04):959-970. |
[5] | Inoue A;Masumoto T;Tomioka H .Microstructure and mechanical properties of rapidly quenched L20 + L20 + L12 alloys in Ni-Al-Co system[J].Journal of Materials Science,1984,19:3097-3106. |
[6] | Kumar K S;Bao G .Intermeatllic matrix composites:an overview[J].Composites Science and Technology,1994,52:127-150. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%