研究含钛量分别为0.22%、0.28%的超低碳氮Cr18不锈钢冷轧板经850℃退火处理后的再结晶组织和再结晶织构,结果表明:含钛0.22%的Cr18不锈钢冷轧板再结晶晶粒尺寸略大于含钛0.28%的Cr18不锈钢冷轧板.含钛0.22%的冷轧板试样在850℃下保温4min时{111}＜112＞取向密度强度达到了16.0,而在相同保温时间,含钛0.28%的冷轧板{111}面织构取向密度强度最大只有12.9.
参考文献
| [1] | 毛卫民;张新明.晶体材料织构定量分析[M].北京:冶金工业出版社,1995 |
| [2] | 李四军,曲家惠,刘刚,王福,左良.退火温度对铁素体区热轧IF钢冷轧板织构的影响[J].钢铁,2006(06):59-62,66. |
| [3] | Bay R K;Jonas J J;Hook R K .Cold rolling and annealing textures in low carbon and extra low carbon steels[J].International Materials Reviews,1994,39(04):129-172. |
| [4] | HOlscher M;Baabe D;Lücke K .Rolling and recrystallization textures of bcc steels[J].STEEL RESEARCH,1991,62:567-575. |
| [5] | 张海兵,王均安,杨光,周邦新,余海峰.Cr11铁素体不锈钢退火过程中织构变化[J].上海金属,2007(04):17-21. |
| [6] | Urabe J;Oriented T .Nucleation and selective growth during the annealing of IF steels[J].ISIJ International,1994,77:94-102. |
| [7] | Wang Z;Wang X .A New Technology to Improve the r-value of Interstitial-Free(IF) Steel Sheet[J].Journal of Materials Processing Technology,2001,113:659-661. |
| [8] | Cornelia Darmann-Nowak;Bernhard Engl .Influence of hotrolling conditions on texture development in deep-drawing steels[J].STEEL RESEARCH,1991,62:576-579. |
| [9] | Bate PS;da Fonseca JQ .Texture development in the cold rolling of IF steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):365-377. |
| [10] | 程国平,茹铮,袁明生.钛、铌添加量对超深冲IF钢板力学性能的影响[J].钢铁,1999(05):47-50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%