珠光体轨道钢是目前我国铁路轨道采用的主要钢种,其性能特点是抗磨损性能好,屈服强度高.珠光体轨道钢在服役时,表面发生损伤,有白蚀层生成,它对钢轨的服役寿命有重大影响.主要介绍了珠光体轨道钢白蚀层的研究进展,从白蚀层的形成过程、组织结构、形成机理等方面进行了阐述.
参考文献
[1] | 苏辉艳.减轻重载列车轮轨磨耗的研究[J].中国铁道科学,1997(06):42-43. |
[2] | 刘启跃,张波,周仲荣.铁路钢轨损伤机理研究[J].中国机械工程,2002(18):1596-1599. |
[3] | 颜秉善;王其昌.钢轨力学与钢轨伤损[M].成都:西南交通大学出版社,1989 |
[4] | Clayton P;Allery M B P.Metallurgical aspects of surface damage problems in rails[J].Canadian Metalurgical Quarterly,1982(21):31-33. |
[5] | Baumann G;Knothe K;Fecht H J .Surface modification,corrugation and nanostructure formation of high speed railway tracks[J].Nano-Structured Materials,1997,9(1-8):751-754. |
[6] | Carroll R I .Rolling contact fatigue of white etching layer:Part 1 Crack morphology[J].Wear,2006,260:119-130. |
[7] | Baumann G;Fecht H J .Formation of white-etching layers on rail treads[J].Wear,1996,191:133-140. |
[8] | Turley D M .Nature of the white-etching surface layers produced during reaming ultra-high strength steel[J].Materials Science and Engineering,1975,19(01):79-86. |
[9] | H.W. Zhang;S. Ohsaki;S. Mitao .Microstructural investigation of white etching layer on pearlite steel rail[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):191-199. |
[10] | W. Lojkowski;M. Djahanbakhsh;G. Burkle;S. Gierlotka;W. Ziclinski;H. -J. Fecht .Nanostructure formation on the surface of railway tracks[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):197-208. |
[11] | Rigney D A;Chen L A .Wear process in sliding systems[J].Wear,1984,100:195. |
[12] | Languillaume J;Kapelski G;Baudelet B.Cementite dissolution in heavily cold drawn pearlitic steel wires[J].Acta Materialia,1996(12):1201. |
[13] | Baumann G .Untersuchungen zu Gefu gestrukturen und Eigenschaften der Weissen Schichten auf verriffelten Schienenlauffla chen[D].Technische Universitat Berlin,1998. |
[14] | Ivanisenko Yu;Lojkowski W .The mechanism of formation of nanostructure and dissolution of cementite in pearlitic steel during high pressure torsion[J].Acta Materialia,2003,51:5555-5570. |
[15] | Osterle W;Rooch H;Pyzalla A .Investigation of white etching layers on rails by optical electron microscopy X-ray and Synchrotron X-ray diffraction[J].Materials Science,2001,A303:150-157. |
[16] | 刘北兴.金属学与热处理原理[M].哈尔滨:哈尔滨工业大学出版社,2005 |
[17] | Yu. Ivanisenko;I. MacLaren;X. Sauvage;R.Z. Valiev;H.-J. Fecht .Phase Transformations in Pearlitic Steels Induced by Severe Plastic Deformation[J].Diffusion and Defect Data. Solid State Data, Part B. Solid State Phenomena,2006(0):133-144. |
[18] | Newcomb S B;Stobbs W M .Transmission electron microscopy study of the white etching layer on a rail head[J].Materials Science and Engineering,1984,66:195. |
[19] | Wang L;Pyzalla A;Stadlbauer W et al.Microstructure features on rolling surfaces of railway rails subjected to heavy loading[J].Materials Science and Engineering,2003,A359:31. |
[20] | Baumann G;Knothe K;Fecht H J.Surface modification,corrugation and nanostructure formation of high speed railway tracks[J].Nano-Structured Materials,1997(09):751. |
[21] | Blackburn L D.Isochronous stress-strain curves for austenitic stainless steels[A].ASME New York,NY,1972:15-48. |
[22] | Fecht H J.[A].Institute of Physics,J.W.Arrowsmith Ltd,1996 |
[23] | 经过严重塑性变形的Armco铁的结构和应变特性[J].Acta materialia,1996(12):4705-4712. |
[24] | Lojkowski W;Grabski M W.[A].,1981:329. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%