在Gleeble-3500热模拟实验机上通过单道次压缩实验,研究了变形温度、应变速率和变形量对TWIP钢流变应力和临界动态再结晶行为的影响规律.结果表明,试验TWIP钢热变形的峰值应力随温度的升高而降低,随着应变速率的增大而升高；各种变形条件下,TWIP钢的奥氏体晶粒尺寸有很大差异,随着变形温度的升高,再结晶晶粒粗化,而应变速率和应变量的增加有利于晶粒细化；最后采用线性回归方法计算出TWIP钢的热变形激活能为443.3 kJ/mol,并求出了该钢种动态再结晶临界条件与Z参数之间的关系,以及动态再结晶动力学规律.
参考文献
| [1] | Graseel O;Frommeyer G;Derder C et al.Phase transformation and mechanical properties of Fe-Mn-Si-Al TRIP-steel[J].Journal De Physique(France)Ⅳ,1977,C5:383-388. |
| [2] | Georg FROMMEYER;Udo BRUX;Peter NEUMANN .Supra-Ductile and High-Strength Manganese-TRIP/TWIP Steels for High Energy Absorption Purposes[J].ISIJ International,2003(3):438-446. |
| [3] | Grassel O.;Frommeyer G.;Meyer LW.;Kruger L. .High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development - properties - application[J].International Journal of Plasticity,2000(10/11):1391-1409. |
| [4] | Zener C;Hollomon J H .Effect of strain rate upon the plastic flow of steel[J].Journal of Applied Physics,1944,15(01):22-32. |
| [5] | S.F.MEDINA;C.A.HERNANDEZ .MODELLING OF THE DYNAMIC RECRYSTALLIZATION OF AUSTENITE IN LOW ALLOY AND MICROALLOYED STEELS[J].Acta materialia,1996(1):165-171. |
| [6] | 刘振宇;许云波;王国栋.热轧钢材组织-性能演变的模拟和预测[M].沈阳:东北大学出版社,2004 |
| [7] | John J. Jonas;Xavier Quelennec;Lan Jiang .The Avrami kinetics of dynamic recrystallization[J].Acta materialia,2009(9):2748-2756. |
| [8] | S.F.MEDINA;C.A.HERNANDEZ .MODELLING OF THE DYNAMIC RECRYSTALLIZATION OF AUSTENITE IN LOW ALLOY AND MICROALLOYED STEELS[J].Acta materialia,1996(1):165-171. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%