镁铬砖由于具有良好的抗热震性和良好的抗渣性,而被广泛应用于冶炼、水泥等高温炉上.自上世纪80年代起,铬公害问题已受到人们的关注,于是开发替代镁铬材料的环境友好型无铬耐火材料成为当今研究的热点.针对当前无铬耐火材料存在的问题,总结了各种无铬耐火材料的研究现状,并讨论了无铬耐火材料未来发展趋势和研究方向.
参考文献
| [1] | 陆纯煊;曾大凡.水泥工业用无铬碱性砖的发展情况[J].水泥,1998(05):11-15. |
| [2] | 陈荣荣;牟济宁;何平显 等.一种真空炉炉衬用无铬耐火材料[P].中国,200410025637.2,2006-01-04. |
| [3] | 宇都重俊 .一种用于金属精炼炉衬的抗热冲击的MgO-ZrO2砖[P].日本,JP63060151 |
| [4] | 杨立志.无铬砖在真空脱气底槽中的应用[J].太钢译文,2003(02):24-26. |
| [5] | Park JH .Formation of CaZrO3 at the interface between CaO-SiO2-MgO-CaF2(-ZrO2) slags and magnesia refractories: Computational and experimental study[J].Calphad: Computer Coupling of Phase Diagrams and Thermochemistry,2007(2):149-154. |
| [6] | 戴彦良.MgO与ZrSiO4反应烧结过程的研究热固性树脂[J].热固性树脂,1999(04):64-67. |
| [7] | 藤谷信吾.二次精炼用无铬化镁尖晶石砖的开发[J].耐火物(日本）,1998(01):17-20. |
| [8] | 陈永强 .直接结合镁铝砖的研究[D].河北理工大学,2005. |
| [9] | Tetsuro Kai;Kyousuke Isaji;Kuniyoshi Torii .Improvement of Magnesia-Spinel Brick for Refining Ladle[J].耐火物,2001(9):521-526. |
| [10] | 王守权;廖建国.MgO-TiO2-Al2O3系骨料的特性[J].Foreign Refractory,2004(07):52-55. |
| [11] | Toyoyasu O;Akiniro T;Isamu S.Application of chrome-free bricks to RH-degasser vessels[A].Berlin,Germany,1999:269-271. |
| [12] | 陈树江 .镁钙系耐火材料将逐渐取代镁铬砖[N].中国建材报,2009. |
| [13] | 陈开献;陈肇友 .混合稀土氧化物与Fe2O3对白云石烧结性能和抗水化性能的影响[J].耐火材料,1992,26(04):187. |
| [14] | 徐延庆;陈肇友 .稀土氧化物对白云石烧结与抗水化性的影响[J].耐火材料,1992,26(05):282. |
| [15] | 顾华志,汪厚植,洪彦若,张文杰,孙加林,欧阳军华.H2C2O4和CO2复合表面处理镁钙砂及其浇注料的性能[J].耐火材料,2005(03):161-164. |
| [16] | Ishii H;Kanatani S.Improvement of magnesia-carbon brick for lower vessel of RH-degassing[A].Osaka,Japan,2003:114-117. |
| [17] | Tamura S;Ochiai T.Nano-tech Refractories-1:The development of the nano-structuralmatrix[A].Osaka,Japan,2003:517-520. |
| [18] | Takanage S;OchiaiT;Tamura S.Nano-tech Refractories-2:The application of the nano structural matrix toMgO-C bricks[A].Osaka,Japan,2003:521-524. |
| [19] | Ochiai T .Development of Refractories by applying nano-techmology[J].Journal of the Technical Association of Refractories,2005,25(01):4-11. |
| [20] | A.S. Gokce;C. Gurcan;S. Ozgen .The effect of antioxidants on the oxidation behaviour of magnesia-carbon refractory bricks[J].CERAMICS INTERNATIONAL,2008(2):323-330. |
| [21] | C.G. ANEZIRIS;J. HUBALKOVA;R. BARABAS .Microstructure evaluation of MgO-C refractories with TiO_2- and Al-additions[J].Journal of the European Ceramic Society,2007(1):73-78. |
| [22] | Kanno Koichi;Koike Nobuyuki;Korai Yozo .Mesophase pitch and phenolic resin blends as binders for magnesia-graphited bricks[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(2):195-201. |
| [23] | Hashemi B;Nemati Z A;Faghihi-Sani M A .Effects of resin and graphite content on density andoxidation behavior of MgO-C refractory bricks[J].Ceramics International,2006,32(03):313-319. |
| [24] | Ganesha I;Bhattacharjeea S;Sahaa B P et al.An efficient MgAl2O4 spinel additive for improved slag erosion and penetration resistance of high-Al2O3 and MgO-C refractories[J].Ceramics International,2002,28(03):245-225. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%