以目前国内外已公开的薄带连铸专利为基础,综述了生产低碳钢薄带产品时微裂纹形成的主要影响因素.采用对钢液的碳、硅、锰、硫的含量进行严格控制；通过真空处理减少钢液中的气体含量；形成足够数量的低熔点夹杂物；采用合适的结晶辊形貌等措施,对于改善结晶辊和铸带之间的传热、减少和控制薄带连铸低碳钢产品的微裂纹缺陷有效果.
参考文献
| [1] | POSCO Constructs New Mass Production System of STS HRC with PoStrip Technology[J].Korea Metal Journal,2010 |
| [2] | Sosinsky D J .The castrip process-recent developments at Nucor steel' s commercial strip casting plant[J].Metallurgist,2008,52(11-12):691-699. |
| [3] | Rama Hahapatra;David Sosiasky .Thin cast steel strip with reduced microcracking[P].US,0175608AI,2007-08-02. |
| [4] | Otsuka Himyuki;Yamane,Koshiro et al.Thin cast steel strip with reduced microcracking[P].WO 2009/021280A1,2007-08-13. |
| [5] | Dan G Edelman;Peter C.Campbell.The Development and Manufacture of Ultra-thin Cast Strip Steel Products with High Residual Elements Levels via the CASTRIP Process[J].AISTech Proceedings-Volume Ⅱ,2011:751-762. |
| [6] | 胡志刚,马春林,刘浏,周英超,路殿华.CSP薄板坯连铸包晶反应区域的研究[J].钢铁研究学报,2006(07):10-13. |
| [7] | 洪兵雄,毛新平,柴毅忠,朱伯平.CSP薄板坯表面纵裂原因及防止措施[J].钢铁钒钛,2004(02):57-61. |
| [8] | Blejde;Walter;Mahapatra et al.Casting steel strip[P].WO 2008/043152A1,2007-10-11. |
| [9] | Geldenhuis;Jacabus;Marthinus et al.Low Cost Making of Low Carbon,Low Suffur,and Low Nitrogen Steel Using Conventional Steelmaking Equipment[P].WO 2010/015020 A1,2010-02-04. |
| [10] | Lazar Strezov .Casting of Metal[P].US,5720336,1998-02-24. |
| [11] | 詹姆斯 G 威廉斯;弗兰克巴巴罗;菲利普 J 伦威克 等.具有高奥氏体晶粒粗化温度的钢制品及其制造方法[P].CN101340990,2011-08-03. |
| [12] | Lazar Strezov .Casting Steel Strip[P].US,6059014,2000-05-09. |
| [13] | Strezov Lazar;Mukunthan Kannappar .Casting Steel Strip[P].WO 00/07753,1999-08-06. |
| [14] | Mahapatra;Rama Ballav;McGaughey et al.Method and apparatus for controlling variable shell thickness in cast strip[P].US,0108228A1,2011-05-12. |
| [15] | Yamamura Hideaki;Hamada Naoya et al.A cooling drum for thin slab continuous casting and continuous casting method thereof[P].EP1602424A1,2001-05-11. |
| [16] | Jeong Seong In;Hwang Suk Kyun .Casting roll with enhanced durability in which a high-rigidity secondary plating layer is formed on a base material of copper alloy and a manufacturing method thereof[P].KR1020080122076,2008-12-03. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%