对单晶硅炉用碳素材料的硅化腐蚀后的表面形貌及元素分布测试,研究不同碳素热场材料的硅化腐蚀性能.结果表明石墨内部延伸至表面的开气孔给熔融硅提供侵蚀扩散的通道,加速石墨硅化破坏.硅化程度受C/C复合材料内部纤维排布方向的影响,沿纤维排布方向液硅扩散速率较快,垂直于纤维排布液硅的扩散速率较小.随硅化时间延长,C/C复合材料力学性能呈下降趋势.石墨材料的力学性能最初有所提高,之后随着时间而下降.
参考文献
| [1] | Jacobson Nathan S;Roth Don J et al.Oxidation through coating crack of SiC-protected carbon/carbon[J].Surface and Coatings Technology,2008,230:372-383. |
| [2] | 赵伟,蔡菲,蔡珣,曹伟伟,朱波.高温石墨炉用碳素材料的热辐射性能研究[J].功能材料,2011(07):1305-1308. |
| [3] | Zhao Wei;Zhu Bo;Chen Yang et al.The oxidation erosion in carbon materials for CZ furnace[J].Advanced Materials Research,2013,602-604:1359-1363. |
| [4] | Roy M.Sullivan .A model for the oxidation of carbon silicon carbide composite structures[J].Carbon: An International Journal Sponsored by the American Carbon Society,2005(2):275-285. |
| [5] | 赵娟,王贵,刘朗,郭全贵.SiC梯度涂层的制备及其氧化行为研究[J].广东化工,2007(10):25-28. |
| [6] | Han K H .Rate of oxidation of carbon fiber/carbon matrix composites with an anti-oxidation at high temperature[J].Journal of the Electrochemical Society,1987,134(04):1003-1009. |
| [7] | 黄剑锋,李贺军,熊信柏,曾燮榕,李克智,付业伟,黄敏.炭/炭复合材料高温抗氧化涂层的研究进展[J].新型炭材料,2005(04):373-379. |
| [8] | 王博 .碳/碳复合材料SiCn-MoSi2/SiC复合抗氧化涂层的制备及性能研究[D].陕西科技大学,2011. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%