采用直流电沉积、脉冲电沉积和超声-脉冲电沉积方法,在45钢表面制备Ni-SiC纳米镀层.研究电沉积方式对Ni-SiC纳米镀层显微组织、成分及耐腐蚀性能的影响.结果表明,超声-脉冲电沉积Ni-SiC纳米镀层显微组织更加致密、光滑.直流电沉积镀层的镍粒径和SiC粒子的平均粒径为175.4和81.5nm;而超声-脉冲电沉积镀层的镍粒径和SiC粒子的平均粒径为74.8和36.3nm.SEM和EDS分析可知,电沉积方式对Ni-SiC纳米镀层的耐腐蚀性能有很大影响,超声-脉冲电沉积镀层的耐腐蚀性能较好.
参考文献
| [1] | Low CTJ;Wills RGA;Walsh FC .Electrodeposition of composite coatings containing nanoparticles in a metal deposit[J].Surface & Coatings Technology,2006(1/2):371-383. |
| [2] | Yin B;Liu G;Zhou H et al.Sliding wear behavior of HVOF-sprayed Cr3C2-NiCr/CeO2 composite coatings at elevated temperature up to 800℃[J].Tribology Letters,2010,37:463-469. |
| [3] | 马春阳,吴蒙华,曲智家.超声波-化学镀Ni-P-SiC纳米复合镀层的工艺研究[J].金属热处理,2011(04):89-92. |
| [4] | Xia, FF;Wu, MH;Wang, F;Jia, ZY;Wang, AL .Nanocomposite Ni-TiN coatings prepared by ultrasonic electrodeposition[J].Current applied physics: the official journal of the Korean Physical Society,2009(1):44-47. |
| [5] | 郑华明,黄新民,何素珍,李鹏,杨明.SiC微粒对电沉积Ni-W-P-SiC复合镀层性能的影响[J].金属功能材料,2010(06):49-54. |
| [6] | Xia F;Xu H;Liu C et al.Microstructures of Ni-AlN composite coatings prepared by pulse electrodeposition technology[J].Applied Surface Science,2013,271:7-11. |
| [7] | 宿辉,蔡伟,曹茂盛.Ni-P-（Ni/SiC）P镀层及其工艺条件的研究[J].材料科学与工艺,2008(03):310-313,318. |
| [8] | 楚广,刘生长.新型Ni-Cu复合镀层的制备[J].中南大学学报（自然科学版）,2007(03):474-479. |
| [9] | 康进兴,赵文轸,徐英鸽,孙立明.电沉积工艺参数对块体纳米晶镍硬度的影响[J].材料工程,2008(07):40-42,46. |
| [10] | 文潮;李迅;孙德玉 等.纳米金刚石颗粒粒度的测量与表征[J].机械科学与技术,2003,7:163-167. |
| [11] | 夏法锋,吴蒙华,贾振元,李智.超声波对纳米Ni-TiN复合镀层的影响[J].功能材料,2008(04):690-691,694. |
| [12] | 胡信国;李桂芝.现代防护装饰性电镀[M].哈尔滨:哈尔滨工业大学出版社,1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%