为制备一种环保型水性纸张防油剂，以丙烯酸单体为溶剂，首先进行异佛尔酮二异氰酸酯(IPDI)、聚醚二醇(PTMG1000)、N-甲基二乙醇胺(MDEA)、全氟烷基乙基醇(FEOH)和丙烯酸羟乙酯(HEA)等的聚氨酯链段的聚合反应，经水乳化分散后，再进行丙烯酸单体的自由基聚合反应，制备了全氟水性聚氨酯-聚丙烯酸酯纸张防油剂。并通过红外光谱(FT-IR)、凝胶渗透色谱(GPC)、热重分析(TG)对聚合物结构性能进行了表征。同时，纸张防水防油应用实验表明，对水和液体石蜡的接触角，可分别达到130.2和113.5°，达到了优异的防水防油效果，并对纸张应用性能进行检测，可以满足日常生活中特种纸的要求。
In order to prepare a kind of environmental friendly waterborne paper water an d oil-resistant agent, the solvent-free perfluoroalkyl waterborne polyurethane-polyacrylate was synthesised.The reaction of polyure-thane by isophorone diisocyanate (IPDI),polytetrahydrofuran ether diol (PTMG1000),N-methyldiethano-lamine (MDEA),perfluorooctyl ethyl alcohol perfluoroalkylol (FEOH)and 2-hydroxyethyl acrylate (HEA) firstly carried out using the acrylic monomers as solvent,and then the radical polymerization of the said acrylic monomers was take place.The structure and performance of the polymer were characterized by Fourier trans-form infrared spectrometer (IR),gel permeation chromatography (GPC),thermogravimetric analysis (TG). At the same,the application of paper water and oil-resistant experiments and paper application performance shown that,the contact angle of water and liquid paraffin were up to 130.2 and 113.5°which indicated that it has excellent water and oil-resistant effect,and it can meet the requirement of specialty paper.
参考文献
| [1] | Reiner Exner .Synthesis and application of polymer sizing agents[J].Paper Technology: The Official Journal of the Paper Industry Technical Association,2002(6):45-51. |
| [2] | 蒋国忠.氟碳防水防油剂的研究进展及发展趋势[J].合成技术及应用,2008(04):37-40. |
| [3] | 王大枋.含氟表面活性剂及其应用[J].杭州化工,2001(02):6-10. |
| [4] | Li H;Zhang ZB;Hu CP;Wu SS;Ying SK .Surface composition and property of film prepared with aqueous dispersion of polyurethaneurea-acrylate including fluorinated block copolymer[J].European Polymer Journal,2004(9):2195-2201. |
| [5] | Li GH;Shen YD;Ren QH .Effect of fluorinated acrylate on the surf ace properties of cationic fluorinated polyurethane-acrylate hybrid dispersions[J].Journal of Applied Polymer Science,2005(6):2192-2196. |
| [6] | 岳杰,沈一丁,赖小娟.PU/PA核壳乳液/水分散异氰酸酯交联成膜机理及其性能研究[J].功能材料,2012(07):851-854. |
| [7] | Yang, J.;Yuan, D.;Zhou, B.;Gao, J.;Ni, H.;Zhang, L.;Wang, X. .Studies on the effects of the alkyl group on the surface segregation of poly(n-alkyl methacrylate) end-capped 2-perfluorooctylethyl methacrylate films[J].Journal of Colloid and Interface Science,2011(1):269-278. |
| [8] | 辛华,李小瑞,沈一丁.聚氨酯-含氟丙烯酸酯防水防油性复合乳液的制备及性能[J].功能材料,2011(03):474-478. |
| [9] | Wang, X.;Ye, Q.;Liu, J.;Liu, X.;Zhou, F. .Low surface energy surfaces from self-assembly of perfluoropolymer with sticky functional groups[J].Journal of Colloid and Interface Science,2010(1):261-266. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%