通过自组装技术在 A l-Mg 合金表面制备自组装分子膜,采用接触角测量仪测定了自组装分子膜的水接触角,采用多功能摩擦磨损试验机对制备不同自组装分子膜的 A l-Mg 合金在3种润滑方式下进行摩擦磨损实验。结果表明,制备自组装分子膜可显著改变Al-Mg 合金的表面润湿性,制备 FDTS、FOTS、OTS自组装分子膜的表面呈疏水性,制备 MPS、APS自组装分子膜的表面则呈亲水性,5种自组装分子膜接触角由大到小的顺序为 FDTS>FOTS>OTS>MPS>APS。自组装分子膜的疏水性越强,Al-Mg 合金的摩擦系数越小。同种自组装分子膜在干摩擦条件下摩擦系数最大,浸水润滑条件下摩擦系数有所下降,喷水润滑条件下摩擦系数最小。
Self-assembled monolayers (SAMs)on Al-Mg alloy surface were prepared by self-assembled tech-nique.Water contact angles on SAMs were measured by contact angle measurement.Tribological characteris-tics of Al-Mg alloy with different SAMs were evaluated by CETR universal micro-tribometer.The results indi-cate that the wettibility of Al-Mg alloy surface can significantly be changed by SAMs.The Al-Mg alloy surfaces with FDTS,FOTS,OTS SAMs appear hydrophobic,however,the Al-Mg alloy surfaces with MPS,APS SAMs posess hydrophilic characteristics.The water contact angles for 5 kinds of SAMs are in the order from large to small,FDTS,FOTS,OTS,MPS,APS.The stronger of hydrophobicity of SAMs,the smaller of friction coef-ficients of Al-Mg alloy.For the same SAMs,the friction coefficient of Al-Mg alloy was lowest in water-j et lu-brication condition,middle in water lubrication condition,and largest in dry friction condition.
参考文献
| [1] | Kang ZX;Mori K;Oishi Y .Surface modification of magnesium alloys using triazine dithiols[J].Surface & Coatings Technology,2005(2/3):162-167. |
| [2] | 李杰,张会臣,高玉周.MB8镁合金疏水/超疏水表面制备与微摩擦特性研究[J].功能材料,2012(22):3063-3069. |
| [3] | Zhixin Kang;Qi Ye;Jing Sang;Yuanyuan Li .Fabrication of super-hydrophobic surface on copper surface by polymer plating[J].Journal of Materials Processing Technology,2009(9):4543-4547. |
| [4] | Jung Y C;Bhushan B .Contact angle,adhesion and fric-tion properties of micro-and nanopatterned polymers for superhydrophbicity[J].Nanotechnology,2006,17:4970-4980. |
| [5] | Zhiguang Guo;Feng Zhou;Jingcheng Hao;Weimin Liu .Stable Biomimetic Super-Hydrophobic Engineering Materials[J].Journal of the American Chemical Society,2005(45):15670-15671. |
| [6] | 康志新,刘应辉,桑静,王芬,李元元,丛培红.Mg-Mn-Ce镁合金表面功能纳米有机薄膜的制备与摩擦学特性[J].摩擦学学报,2011(01):12-17. |
| [7] | 赵文杰,黄德明,王立平,薛群基.链长对离子液体超薄膜微/纳摩擦学性能的影响[J].摩擦学学报,2010(06):614-619. |
| [8] | M. Ratoi;H. A. Spikes .Lubricating properties of aqueous surfactant solutions[J].Tribology Transactions,1999(3):479-486. |
| [9] | Boschkova K;Kronberg B;Rutland M et al.Studr of thin surfactant films under shear using the tribological surface force apparatus[J].Tribology International,2001,34:815-822. |
| [10] | Sakuma H;Otsuki K;Kurihara K .Viscosity and lubricity of aqueous NaCl solution confined between mica surfaces studied by shear resonance measurement[J].Physical review letters,2006(4):6104-1-6104-4-0. |
| [11] | U. Srinivasan;M. R. Houston;R. T. Howe;R. Maboudian .Alkyltrichlorosilane-based self-assembled monolayer films for stiction reduction in silicon micromachines[J].Journal of Microelectromechanical Systems: A Joint IEEE and ASME Publication on Microstructures, Microactuators, Microsensors, and Microsystems,1998(2):252-260. |
| [12] | Nakagawa T;Soga M .Contact angle and atomic force microscopy study of reactions of n-alkyltrichlorosilanes with muscovite micas exposed to water vapor plasmas with various power densities[J].Japanese Journal of Applied Physics,1997,36:6915-6921. |
| [13] | Tsukruk V V;Everson M P;Lander L M et al.Nano-tribo-iogical properties of composite molecular films:C60 anchored to a self-assembled monolayer[J].Langmuir,1996,12:3905-3911. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%