以 NH4 H2 PO4为活化剂,采用物理-化学活化法对玉米秸秆活性炭的制备进行了系统研究；对制备出的活性炭进行羟基磷灰石(HAP)负载,并对负载H AP活性炭的水中氟离子吸附动力学、热力学进行了研究。结果表明,优化工艺条件为浸渍比1∶4、活化温度700℃、活化时间60min。负载 HAP 活性炭较活性炭比表面积减小约1倍,但除氟能力增加14倍。升高温度有利于吸附的进行,负载 H AP 活性炭吸附过程更符合 Langmuir 吸附模型。吸附过程中ΔG<0,ΔH 为20.08kJ/mol,ΔS 为72.14J/(mol·K)。吸附过程符合一级动力学模型。
Corn straw activated carbon was prepared with NH4 H2 PO4 as activator by the physical-chemical acti-vation method,which was researched systematically.Hydroxyapatite (HAP)was loaded on the preparation of the activated carbon,and fluoride ion adsorption of the activated carbon supported HAP dynamics,thermody-namics was studied.The results showed that the optimized process conditions were 1∶4 of dipping ratio,700℃of activation temperature,60 minutes of activation time.The specific surface area of the activated carbon sup-ported HAP was half of the activated carbon,but the suction fluorine ability increased 14 times.High tempera-ture was conducive to adsorption,adsorption process of activated carbon supported HAP was more suitable to Langmuir adsorption model.ΔG was less than zero in adsorption process,ΔH was 20.08kJ/mol andΔS was 72.14J/(mol·K).Kinetic experiments showed that the adsorption process was in line with the level of dynam-ic model.
参考文献
| [1] | Rashidi N A;Yusup S et al.Activate carbon from the re-newable agricultural residues using single step physical activation:a preliminary analysis[J].APCBEE Procedia,2012,3:84-92. |
| [2] | Kadirvelu K.;Kavipriya M.;Karthika C.;Radhika M.;Vennilamani N. Pattabhi S. .Utilization of various agricultural wastes for activated carbon preparation and application for the removal of dyes and metal ions from aqueous solutions[J].Bioresource Technology: Biomass, Bioenergy, Biowastes, Conversion Technologies, Biotransformations, Production Technologies,2003(1):129-132. |
| [3] | O. Ioannidou;A. Zabaniotou .Agricultural residues as precursors for activated carbon production—A review[J].Renewable & sustainable energy reviews,2007(9):1966-2005. |
| [4] | 王广建,张健康,杨志坚,刘英环.活性炭负载银吸附剂的制备与脱除苯并噻吩的研究[J].功能材料,2013(07):949-953. |
| [5] | 李湘洲.磷酸法制备棉秆活性炭的研究[J].林业科学,2005(05):115-117. |
| [6] | Subhashini Ghorai;K.K.Pant .Equilibrium,kinetics and breakthrough studies for adsorption of fluoride on activated alumina[J].Separation and Purification Technology,2005(3):265-271. |
| [7] | Popat K M;Anand P S;Dasare B D .Selective removal of fluoride ions from water by the aluminum form of the aminomethylphosphonic acid-type ion exchanger[J].Re-act Polym,1994,23(01):23-32. |
| [8] | 孟紫强,耿红,刘海龙.6种吸附材料饮水除氟效果的比较研究[J].中国地方病学杂志,2002(05):373-376. |
| [9] | 王鼎.粉末状骨炭用于饮用水除氟的试验研究[J].水资源保护,2008(01):63-64,68. |
| [10] | 谢虹,贾文波,吴志刚.活性氧化铝除氟剂的除氟性能研究[J].华中科技大学学报（医学版）,2005(05):644-646. |
| [11] | R. Leyva-Ramos;J. Rivera-Utrilla;N.A. Medellin-Castillo .Kinetic modeling of fluoride adsorption from aqueous solution onto bone char[J].Chemical engineering journal,2010(3):458-467. |
| [12] | G. Alagumuthu;M. Rajan .Equilibrium and kinetics of adsorption of fluoride onto zirconium impregnated cashew nut shell carbon[J].Chemical engineering journal,2010(3):451-457. |
| [13] | Viswanathan N;Meenakshi S .Enhanced fluoride sorption using La(III) incorporated carboxylated chitosan beads[J].Journal of Colloid and Interface Science,2008(2):375-383. |
| [14] | Khan A;Singh R .Adsorption thermodynamics of carbo-furan on Sn(IV)arsenosilicate in H+,Na+ and Ca2+forms[J].Colloids and Surfaces,1987,24(01):421-427. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%