等离子体类聚氧乙烯薄膜(PEO-like)具有高亲水性、抗生物粘附的特性,能被应用于生物材料表面改性以提高材料的抗蛋白粘附、抗血小板粘附和抗菌等性能。以四乙二醇二甲醚(tetraethylene glycol dimethyl ether)为单体,采用射频等离子体连续放电模式,不锈钢 SS 为基底,在不同功率下合成了 PEO-like薄膜。傅里叶变换红外光谱仪(FT-IR)、X光电子能谱仪(XPS)测试分析表明等离子体 PEO-like 薄膜中能部分保留单体分子中的氧化乙烯(EO)结构单元,功率为5 W合成的 PEO-like 薄膜中 EO 单元含量为35.86%。PEO-like 薄膜的亲水性优于不锈钢,薄膜在双蒸水中浸没1和10d 的结果显示,尽管薄膜出现溶胀现象,但没有剥落和破裂。低功率下合成的薄膜具有一定的阻抗血小板粘附的性能,但3d的体外平滑肌细胞评价结果表明,3种 PEO-like 薄膜没有表现出抑制平滑肌细胞增殖的性能。
The polyethylene oxide like (PEO-like)film prepared by plasma polymerization has high hydrophilici-ty and anti-bioadhesion,which can be used to modify the biomaterial surface to improve the inhibition of protein adhesion,platelet adhesion and anti-bacterial adhesion.The PEO-like films on stainless steel (SS)substrates were prepared by radio frequency plasma polymerization technique with tetraethylene glycol dimethyl ether (EGDME)as the precursor.The results of Fourier transform infrared spectroscopy (FT-IR)and X-ray photoe-lectron spectroscopy (XPS)showed that the PEO-like film could keep part of ethylene oxide unit,and especial-ly the EO content of PP-PEO-1 film fabricated under 5W power was 35.86%.Compared to the SS,there was more hydrophilic for the PEO-like films.The PEO-like films exhibited the swollen stripes,but the spalling and rupture could not be found.The PEO-like film prepared under 5W and 10W had certain properties to prohibit the adhesion of platelet.But the evaluation of in vitro smooth muscle cell (SMC)cultured for 3 days indicated that three kinds of PEO-like films had not shown the significant prohibition of SMC.
参考文献
| [1] | Vincent Zoulalian;Stefan Zurcher;Samuele Tosatti;Marcus Textor;Sophie Monge;Jean-Jacques Robin .Self-Assembly of Poly(ethylene glycol)-Poly(alkyl phosphonate)Terpolymers on Titanium Oxide Surfaces: Synthesis, Interface Characterization, Investigation of Nonfouling Properties, and Long-Term Stability[J].Langmuir: The ACS Journal of Surfaces and Colloids,2010(1):74-82. |
| [2] | Hamilton-Brown, P;Gengebach, T;Griesser, HJ;Meagher, L .End Terminal, Poly(ethylene oxide) Graft Layers: Surface Forces and Protein Adsorption[J].Langmuir: The ACS Journal of Surfaces and Colloids,2009(16):9149-9156. |
| [3] | Marga C. Lensen;Petra Mela;Ahmed Mourran .Micro- and Nanopatterned Star Poly(ethylene glycol) (PEG) Materials Prepared by UV-Based Imprint Lithography[J].Langmuir: The ACS Journal of Surfaces and Colloids,2007(14):7841-7846. |
| [4] | Cao L;Chang M;Lee CY;Castner DG;Sukavaneshvar S;Ratner BD;Horbett TA .Plasma-deposited tetraglyme surfaces greatly reduce total blood protein adsorption, contact activation, platelet adhesion, platelet procoagulant activity, and in vitro thrombus deposition.[J].Journal of biomedical materials research, Part A,2007(4):827-837. |
| [5] | Jayakrishnan A .Chemical modification of poly(vinyl chloride) resin using poly(ethylene glycol) to improve blood compatibility.[J].Biomaterials,2005(17):3495-3502. |
| [6] | Benesch J;Svedhem S;Svensson S C T et al.Protein adsorption to oligo(ethylene glycol)self-assembled mon-olayers:experiments with fibrinogen,heparinized plas-ma,and serum[J].Journal of Biomaterials Science Pol-ymer Edition,2001,12(06):581-589. |
| [7] | Hou Ruixia;Wu Leigang;Wang Jin et al.Investigation on biological properties of tacrolimus-loaded poly(1,3-trimethylene carbonate)in vitro[J].Applied Surface Sci-ence,2010,256:5000-5005. |
| [8] | Choukourov A;Gordeev I;Polonskyi O et al.Poly(eth-ylene oxide)-like plasma polymers produced by plasma-assisted vacuum evaporation[J].Plasma Processes and Polymers,2010,7:445-458. |
| [9] | Sardella E;Gristina R;Senesi G S et al.Homogeneous and micro-patterned plasma-deposited PEO-like coatings for biomedical surfaces[J].Plasma Processes and Poly-mers,2004,1:63-72. |
| [10] | Touzin M;Chevallier P;Lewis F;Turgeon S;Holvoet S;Laroche G;Mantovani D .Study on the stability of plasma-polymerized fluorocarbon ultra-thin coatings on stainless steel in water[J].Surface & Coatings Technology,2008(19):4884-4891. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%