以EDTA-2Na为螯合剂,在不同pH条件下,采用水热法制备得到了不同形貌的CoS2,利用X射线衍射(XRD)、扫描电子显微镜(SEM)、激光粒度分布仪对产物进行了表征,最后将不同形貌的CoS2装配成单体电池进行放电测试.实验结果表明,在酸性条件(pH值=1、4)下制备的CoS2呈空心球形,在中性条件(pH值=7)下制备的CoS2呈表面带有大量纳米级颗粒的块状,在碱性条件(pH值=9、11)下制备的CoS2呈片状.随pH值的增大,CoS2材料的粒度逐渐减小,单体电池的放电平台电压逐渐升高,内阻减小.
参考文献
[1] | 陆瑞生;刘效疆.热电池[M].北京:国防工业出版社,2005:267. |
[2] | 兰伟,李立.热电池新技术的研究进展[J].电池工业,2008(06):405-408. |
[3] | Guidotti R A;Reinhardt F W;Dai J et al.Performance of thermal cells and batteries made with plasma-sprayed cathodes and anodes[J].Journal of Power Sources,2006,160(02):1456-1464. |
[4] | Guidotti R A;Nigrey P J;Reinhardt F W.Preparation and characterization of synthetic CoS2 for use in thermal battery[A].New Jersey,2004:149-152. |
[5] | 苑晓宇,马伟民,闻雷,杨化仁.热电池正极材料的研究进展[J].陶瓷学报,2010(04):663-669. |
[6] | Qian XF.;Wang C.;Tang KB.;Xie Y.;Qian YT.;Zhang XM. .Solvent-thermal preparation of nanocrystalline pyrite cobalt disulfide[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1998(1/2):110-112. |
[7] | Qian XF.;Xie Y.;Qian YT.;Li YD. .The synthesis and morphological control of nanocrystalline pyrite nickel disulfide and cobalt disulfide[J].Materials Chemistry and Physics,2000(1):97-99. |
[8] | 王敏,闵宇霖,张元广,陈友存.水热法制备二硫化钴空心微球[J].化学世界,2009(10):577-579,589. |
[9] | 张玲,郑毓峰,孙言飞,董有忠.晶种诱导水热合成二硫化钴CoS2粉体及结构精修[J].新疆大学学报(自然科学版),2006(01):47-52. |
[10] | 谢玲玲,吴荣,李锦,孙言飞,简基康.pH值对水热合成黄铁矿型CoS2微晶的影响[J].无机化学学报,2011(01):95-99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%