通过固相和溶胶-凝胶法分别制备了尖晶石结构的 Cu1．1 Mn1．9 O 4粉末.Cu1．1 Mn1．9 O 4材料750℃的电导率为30 S/cm,室温~800℃加热和冷却有少量第二相溶入和析出,与 SOFC 阴极材料 La0．8 Sr0．2 MnO 3(LSM)在750℃/500 h 共烧时表现出很好的化学稳定性.
Cu1 .1 Mn1 .9 O 4 powder was prepared by solid reaction method and sol-gel method.The electrical conduc-tivity of Cu1 .1 Mn1 .9 O 4 powder was 30 S/cm at 750 ℃,and a small amount of second phase was dissolved and precipitated from it in heating and cooling process when the temperature rising from RT to 800 ℃ or decreasing from 800 ℃ to RT.It showed a good chemical stability when Cu1 .1 Mn1 .9 O 4 sintered with La0.8 Sr0.2 MnO 3 (LSM) for 500 h at 500 ℃.
参考文献
| [1] | Zhu WZ.;Deevi SC. .Development of interconnect materials for solid oxide fuel cells [Review][J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):227-243. |
| [2] | Yang Z G;Weil K S;Paxton D M et al.Selection and evaluation of heat-resistant alloys for SOFC interconnects applications[J].Journal of the Electrochemical Society,2003,150(09):A1181-A1201. |
| [3] | Fergus JW .Metallic interconnects for solid oxide fuel cells[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):271-283. |
| [4] | 郭晓霞,郑文君,孟广耀.固体氧化物燃料电池连接材料的研究进展[J].功能材料,2000(01):23-25. |
| [5] | Tu Hengyong;Stimming U .Advances,aging mecha-nisms and lifetime in solid-oxide fuel cells[J].Journal of Power Sources,2004,127:284-293. |
| [6] | Andre L.G. Prette;Marco Cologna;Vincenzo Sglavo;Rishi Raj .Flash-sintering of Co_2MnO_4 spinel for solid oxide fuel cell applications[J].Journal of Power Sources,2011(4):2061-2065. |
| [7] | Xu Y;Wen Z;Wang S et al.Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC in-terconnects applications[J].Solid State Ionicis,2010,192(01):561-564. |
| [8] | Zhenguo Yang;Guan-Guang Xia;Xiao-Hong Li;Jeffry W. Stevenson .(Mn,Co)_3O_4 spinel coatings on ferritic stainless steels for SOFC interconnect applications[J].International journal of hydrogen energy,2007(16):3648-3654. |
| [9] | Bertoldi M;Zandonella T;Montinaro D et al.Protective coatings for metallic interconnects for IT-SOFC applica-tion[J].JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY,2008,5(01):011001.1-011001.5. |
| [10] | Reza Bateni M;Wei Ping;Deng Xiaohua et al.Spinel coating for UNS 430 stainless steel interconnects[J].Surface and Coatings Technology,2007,201(08):4677-4684. |
| [11] | K.A. Nielsen;M. Solvang;S.B.L. Nielsen .Glass composite seals for SOFC application[J].Journal of the European Ceramic Society,2007(2/3):1817-1822. |
| [12] | Anthony Petric;Hang Ling .Electrical Conductivity and Thermal Expansion of Spinels at Elevated Temperatures[J].Journal of the American Ceramic Society,2007(5):1515-1520. |
| [13] | Stanislowski M;Froitzheim J;Niewolak L .Reduction of chromium vaporization from SOFC interconnects by highly effective coatings[J].Journal of Power Sources,2007,164(02):578-589. |
| [14] | HUA Bin,KONG YongHong,LU FengShuang,ZHANG JianFu,PU Jian,LI Jian.The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect[J].科学通报（英文版）,2010(33):3831-3837. |
| [15] | Zigui Lu;Jiahong Zhu;E. Andrew Payzant .Electrical Conductivity of the Manganese Chromite Spinel Solid Solution[J].Journal of the American Ceramic Society,2005(4):1050-1053. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%