采用间接超声搅拌方式电化学沉积生长了微棱镜反光材料工作模。研究了间接超声电沉积带来的温升原因，以及温升和空化综合作用对工作模反光性能的影响。采用 X 射线衍射对电沉积镍层的结构进行分析，逆反射标志测量仪测量了镍铸层的表面反光系数，并采用3D 激光电子扫描显微镜观测了镍铸层的表面形貌和微棱侧面粗糙度。结果表明，在间接超声作用下，随着时间的增加，电解液温度单调增加，工作模侧面粗糙度和反光系数呈现折线变化。低频时，超声空化起主要作用；高频时，超声温升起主要作用。在70 kW/m2和40 kHz 时，工作模的粗糙度最低，反光系数最高。
Working mould with microprism structure of reflecting material was fabricated by indirect-ultrasonic electrochemical deposition.Temperature rise reason at indirect-ultrasonic electrochemical deposition was inves-tigated.Combined influence of temperature rise and cavitation on reflective performance of working mould was studied.X-ray diffraction,retroreflectometer and 3D laser scanning microscopy system were used to analysis the structure,surface retroreflective coefficient,surface morphology and surface roughness of the casting films. The results show that electrolyte temperature was increased when increasing the time by using indirect-ultra-sonic.Surface retroreflective coefficient and roughness of working mould were increased first and then decreased when increasing the ultrasonic power.Ultrasonic cavitations account for a maj or role under low frequency,and ultrasonic temperature plays a main role under high frequency.Also,when the intensity of sound was 70 kW/m2 and the frequency was 40 kHz,the roughness of working mould was minimum and surface retroreflective co-efficient was maximum.
参考文献
| [1] | Robert W .Ultrasound and Electroplating[J].CHEMISTRY IN BRITAIN,1990,26(03):251-254. |
| [2] | Christo N.Nanev;Anita Penkova .Nucleation of lysozyme crystals under external electric and ultrasonic fields[J].Journal of Crystal Growth,2001(1/4):285-293. |
| [3] | 吴蒙华,傅欣欣,李智,夏法锋.超声电沉积镍/纳米碳化硅复合镀层组织结构研究[J].机械工程材料,2004(12):46-48. |
| [4] | E.Dalas .The effect of ultrasonic field on calcium carbonate scale formation[J].Journal of Crystal Growth,2001(1/2):287-292. |
| [5] | 夏法锋,吴蒙华,贾振元,李智.超声波对纳米Ni-TiN复合镀层的影响[J].功能材料,2008(04):690-691,694. |
| [6] | Jensen JAD.;Pocwiardowski P.;Persson POA.;Hultman L.;Moller P. .Acoustic streaming enhanced electrodeposition of nickel[J].Chemical Physics Letters,2003(5-6):732-737. |
| [7] | Amara N.;Ratsimba B.;Wilhelm A.;Delmas H. .Growth rate of potash alum crystals: comparison of silent and ultrasonic conditions[J].Ultrasonics sonochemistry,2004(1):17-21. |
| [8] | Kenneth S Suslick;Gareth J Price .APPLICATIONS OF ULTRASOUND TO MATERIALS CHEMISTRY[J].Annual review of materials research,1999(0):295-326. |
| [9] | Chow R;Blindt R;Chivers R;Povey M .A study on the primary and secondary nucleation of ice by power ultrasound[J].Ultrasonics,2005(4):227-230. |
| [10] | Watanabe T;Cheng Zhuping;Yang Guang.Nano-plat-ing[M].北京:化学工业出版社,2006:52-54. |
| [11] | Feng Ruo.Ultrasonic diagnostic equipment principle and design[M].Beijing:Chinese Medical Science and Tech-nology Press,1993:68-72. |
| [12] | Li H;Li HR;Guo ZC;Liu Y .The application of power ultrasound to reaction crystallization[J].Ultrasonics sonochemistry,2006(4):359-363. |
| [13] | 杭方学,丘泰球,贲永光.声结晶技术的研究进展[J].声学技术,2007(03):539-544. |
| [14] | 明平美,朱荻,胡洋洋,曾永彬.超声微细电铸试验研究[J].中国机械工程,2008(06):644-647. |
| [15] | Yang Yanling;Shen Yongfeng;Chen Jingeng et al.Nanocrystallne nickelcoating prepared by pulsed electro-deposition combined with ultrasonic agitation[J].ACTA METALLURGICA SINICA,2007,43(08):883-888. |
| [16] | Li Daibing .Study on micro-electroforming process and surface quality of microlens arrays nickel mold inset[D].Hunan:Central South University,2011. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%