以尿素为致孔剂制备了海藻酸钙(CA)水凝胶过滤膜，测试了其通量、截留率和力学性能；通过扫描电子显微镜(SEM)观测其过滤硫酸钙前后的表面形貌.结果表明，增加尿素含量，均导致膜应力和应变的下降；而膜的纯水通量则迅速增大，尿素含量为3．0％(质量分数)时达到28．7 L/(m2·h)，为最大；0．2 MPa下，过滤1．7 g/L 硫酸钙时对 Ca2＋和 SO 2－4的截留率分别为83％和92％，稳定通量达到21．7 L/(m2·h).
In this thesis,urea was used as a porogen to prepare calcium alginate (CA)hydrogel filtration mem-brane.The flux,retention and mechanical properties of the CA filtration membrane were tested.The surface morphology of CA filtration membrane before and after filtrating calcium sulphate was observed by scanning e-lectron microscopy (SEM).Results showed that the stress and strain of the membrane reduced with the increase of urea content.When the concentration of urea was less than 2.5wt%,the water flux of membrane increased rapidly with the increase of urea content.When the urea was 3.0wt%,the flux reached 28.7 L/(m2 ·h).With the continue increase of the urea amount the flux increased little.When the pressure was fixed at 0.2 MPa,the retention rate of Ca2 + and SO 2 -4 for the CA filtration membrane was 83% and 92%,respectively.And the stable flux reached 21.7 L/(m2 ·h).
参考文献
| [1] | Pontalier P Y;Ghoul A I M .Mechanisms for the selective rejection of solutes innanofiltration membranes[J].Sepa-ration and Purification Technology,1997,12(03):175-181. |
| [2] | 楼民,俞三传,高从堦.纳滤在水处理中的应用研究进展[J].工业水处理,2008(01):13-17. |
| [3] | 邓慧宇,徐又一,朱利平,魏秀珍,朱宝库.树状聚合物PAMAM制备高脱盐纳滤膜[J].功能材料,2011(05):793-798. |
| [4] | Chen Bing;Zhang Chunhua;Yang Fenglin et al.Prepa-ration and performance of polyvinyl alcohol ceramic com-posite[J].Membranes Technology of Water Treatment,2006,32(10):17-20. |
| [5] | Wang XF;Fang DF;Yoon K;Hsiao BS;Chu B .High performance ultrafiltration composite membranes based on poly(vinyl alcohol) hydrogel coating on crosslinked nanofibrous poly(vinyl alcohol) scaffold[J].Journal of Membrane Science,2006(1/2):261-268. |
| [6] | Peppas NA;Bures P;Leobandung W;Ichikawa H .Hydrogels in pharmaceutical formulations.[J].European journal of pharmaceutics and biopharmaceutics: official journal of Arbeitsgemeinschaft fuer Pharmazeutische Verfahrenstechnik e.V,2000(1):27-46. |
| [7] | 陈晓琳,王铎,王伟伟,高从堦.海藻酸钠/聚砜复合纳滤膜的研究[J].中国海洋大学学报（自然科学版）,2010(10):85-89. |
| [8] | 沈江南,俞昌朝,阮慧敏,曾淦宁.海藻酸钠/聚砜复合纳滤膜的制备与性能研究[J].水处理技术,2011(07):37-40. |
| [9] | 郝晓丽,夏延致,纪全,孔庆山,隋坤艳.海藻酸钙多孔支架的制备研究[J].功能材料,2009(10):1703-1704,1708. |
| [10] | GB/T 13025.6-1991,Common test methods for indus-trial salt,determination of calcium and magnesium ions[S]. |
| [11] | Huang R.Y.M.;Moon G.Y.;Pal R. .Characteristics of sodium alginate membranes for the pervaporation dehydration of ethanol-water and isopropanol-water mixtures[J].Journal of Membrane Science,1999(1):101-113. |
| [12] | Li Xiaoming;Wang Duo;Gao Xueli et al.Study on performance of nanofiltration membrane for seawater softening and membrane fouling[J].Membranes Tech-nology of Water Treatment,2008,34(04):8-11. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%