通过溶胶凝胶法在聚四氟乙烯(PTFE)平板微孔膜表面形成Si O 2微纳米粒子,再采用全氟癸基三甲氧硅烷(FAS-17)对其进行修饰,获得超疏水表面的PTFE平板微孔膜.考察了正硅酸乙酯(TEOS)和三甲基三乙氧基硅烷(MTES)配比、FAS-17浓度等对平板膜疏水性和微孔结构的影响,并研究了其膜蒸馏性能.结果表明,改性后 Si O 2纳米粒子可均匀附着和内嵌在膜的原纤-结点网络结构内；当 MTES/TEOS 的比例和 FAS-17浓度增大时,膜表面静态接触角(WCA)先增加后减小,膜孔径和孔隙率也随之减小；当MTES/TEOS的比例为1∶1,FAS-17浓度为4％(质量分数)时,改性膜的 WCA 达到154°,滚动角(RA)为8°,达到超疏水效果；由于超疏水作用,改性膜在膜蒸馏运行过程中膜污染程度降低,产水通量恒定在3．65 kg/h·m2左右,脱盐率保持99．8％以上.
The polytetrafluoroethylene (PTFE)flat-sheet membrane with superhydrophobic surface was pre-pared by the formation of SiO2 nanoparticles on the surface of virgin membrane through the sol-gel method and the modification of perfluorodecyl trimethoxy silane (FAS-17)on the surface of SiO2 nanoparticles.The effects of ratio of tetraethyl orthosilicate (TEOS)and Trimethyl triethoxy silane (MTES)and the concentration of FAS-1 7 on the hydrophobility and microstructure of the membrane were studied.The membrane distillation property of the superhydrophobic modified membrane was also investigated.The results showed that the SiO2 nanoparticles adhered and embedded in the network structures of nodes interconnected by fibrils.The surface water contact angle (WCA)of membrane increased maximum and then decreased with the increase of the ratio of TEOS and MTES and the concentration of FAS-17.However,the pore size and porosity of membrane de-creased with the increase of the ratio of TEOS and MTES and the concentration of FAS-17.When the ratio of TEOS and MTES and the concentration of FAS-1 7 were 1∶1 and 4wt%,respectively,the WCA and rolling an-gle were 154 and 8°,respectively.The result of membrane distillation test showed that the modified membrane suffered less membrane fouling compared to the virgin membrane due to superhydrophobic modification.The permeate flux of the modified membrane maintained at about 3.65 kg/h??m2 over the testing period and the salt rej ection was more than 9 9 .8%.
参考文献
| [1] | Xiaosheng Ji;Efrem Curcio;Sulaiman Al Obaidani .Membrane distillation-crystallization of seawater reverse osmosis brines[J].Separation and Purification Technology,2010(1):76-82. |
| [2] | Abdullah Alkhudhiri;Naif Darwish;Nidal Hilal.Membrane distillation: A comprehensive review[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2012:2-18. |
| [3] | Saffarini R B;Mansoor B;Thomas R et al.Effect of temperature-dependent microstructure evolution on pore wetting in PTFE membranes under membrane distillation conditions[J].Journal of Membrane Science,2013,429:282-294. |
| [4] | Marek Gryta .Long-term performance of membrane distillation process[J].Journal of Membrane Science,2005(1/2):153-159. |
| [5] | Erbil H Y;Demirel A L;Avc?Y et al.Transformation of a simple plastic into a superhydrophobic surface[J].SCIENCE,2003,299:1377-1380. |
| [6] | 郑傲然,周明,杨加宏.仿生超疏水表面的制备及润湿性研究[J].功能材料,2007(11):1874-1876,1883. |
| [7] | Nishimoto S;Bhushan B .Bioinspired self-cleaning sur-faces with superhydrophobicity,superoleophobicity,and superhydrophilicity[J].Rsc Advances,2013,3:671-690. |
| [8] | Razmjou A;Arifin E;Dong G et al.Superhydrophobic modification of TiO2 nanocomposite PVDF membranes for applications in membrane distillation[J].Journal of Membrane Science,2012,415:850-863. |
| [9] | Shengyang Yang;Su Chen;Yuan Tian .Facile Transformation of a Native Polystyrene (PS) Film into a Stable Superhydrophobic Surface via Sol-Gel Process[J].Chemistry of Materials: A Publication of the American Chemistry Society,2008(4):1233-1235. |
| [10] | 赵存挺,冯新星,吴芳,陈建勇.单分散纳米二氧化硅微球的制备及羧基化改性[J].功能材料,2009(11):1942-1945. |
| [11] | Meihua Jin;Xinjian Feng;Lin Feng;Taolei Sun;Jin Zhai;Tiejin Li;Lei Jiang .Superhydrophobic Aligned Polystyrene Nanotube Films with High Adhesive Force[J].Advanced Materials,2005(16):1977-1981. |
| [12] | Salapare, H.S.;Guittard, F.;Noblin, X.;Taffin de Givenchy, E.;Celestini, F.;Ramos, H.J..Stability of the hydrophilic and superhydrophobic properties of oxygen plasma-treated poly(tetrafluoroethylene) surfaces[J].Journal of Colloid and Interface Science,2013:287-292. |
| [13] | 钱斯文,王建方,吴文健.纳米微结构涂层的制备及其超疏水性研究[J].功能材料,2008(12):2053-2056. |
| [14] | Khayet M.;Mengual JI.;Godino P. .Theory and experiments on sweeping gas membrane distillation[J].Journal of Membrane Science,2000(2):261-272. |
| [15] | Chul Haeng Lee;Won Hi Hong .Effect of operating variables on the flux and selectivity in sweep gas membrane distillation for dilute aqueous isopropanol[J].Journal of Membrane Science,2001(1):79-86. |
| [16] | Facile preparation of super-hydrophobic and super-oleophilic silica film on stainless steel mesh via sol-gel process[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2010(13):p.4095. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%