利用超声波细胞粉碎机对水解胶原蛋白进行预处理，通过 FT-IR、XRD、TG 等手段测定超声波处理前后胶原蛋白结构的变化，结果表明，超声波处理并不改变胶原蛋白的结构。利用纳米粒度仪测定超声波处理时间和处理功率对胶原蛋白粒径的影响，以及超声波处理前后胶原蛋白的粒径分布，实验结果表明，超声波处理时间和功率在一定的范围内的确可以改变胶原蛋白的粒径，超过范围后则影响较小；超声波处理过程中，胶原蛋白大分子逐渐变为小分子，小分子通过氢键与大分子结合。利用处理过的胶原蛋白合成施胶剂，然后对瓦楞原纸进行表面施胶，通过考察施胶后纸张的性能，得到合成施胶剂的粒径与施胶后纸张的性能呈现相关性。
The ultrasonic cell crusher was used to pretreated of hydrolyzed collagen,collagen structure changes before and after ultrasound were measured by FT-IR,XRD,TG,the results shows that ultrasound does not change the structure of collagen.The influence of particle size and particle size distribution of collagen,before and after ultrasonic with different ultrasonic time and ultrasonic power,were measured by using nano-particle size,experimental results show that ultrasonic time and power in a certain range can indeed change the particle size of collagen,and less affected when the scope was exceed.In ultrasonic process,the collagen molecules into small molecules,while small molecules bonding with macromolecules by hydrogen.The hydrolyzed collagen af-ter ultrasonic treatment were modified to get a sizing agent,and then be used for paper surface sizing,by inves-tigating the performance of paper after sizing,to find out the relationship between the particle size of synthetic sizing agent and sizing performance of the sheets after sizing.
参考文献
| [1] | 丁绍兰,秦宁.皮革固体废弃物资源化处理与处置[J].西部皮革,2009(11):20-24. |
| [2] | Alexander K T W;Corning D R;Cory N J et al.Envi-ronmental and safety issue-cleans technology and envi-ronmental auditing[J].Soc Leather Tech Chem,1992,76:17-23. |
| [3] | 彭立新,王志杰.胶原蛋白的提取及在造纸中的应用[J].中国皮革,2007(05):49-51. |
| [4] | Wang Y L .Dechromization of waste clastic chroming skin[J].China Leather,1990,19(10):4-8. |
| [5] | Li D;Li G Y;Jiang D Y et al.Study on interaction be-tween copolymer(acrylic acid-butenoic aldehyde)and picking pig skin[J].China Leather,2008,37(09):8-11. |
| [6] | Cantera C S .Hydrolysis of chrome shavings:application of collagen hydrolyzate and "Acrylic-Protein”in post tan-ning operation[J].Soc Leather Tech Chem,1997,81(5):183-191. |
| [7] | Fan H J;Shi B;Li L et al.Modification of gelatin for series leather chemicals[J].Leather Chemicals,1999,16(5):12-13. |
| [8] | 周巍,赵鹏,林超,文学军,徐红珍,张荣华.胶原蛋白纳米超薄膜在生物材料表面的原位构建及表征[J].功能材料,2012(21):3010-3013,3017. |
| [9] | 陈永芳,丁志文.胶原蛋白接枝共聚改性的研究[J].中国皮革,2007(23):24-26. |
| [10] | Jin Y;Dong Y;Wei D Q .Acrylic-butane aldehyde co-polymer interact with leather research[J].China Leath-er,2007,36(05):26-29. |
| [11] | Madera-Santana TJ.;Lucero AM.;Torres AC. .Extrusion and mechanical characterization of PVC leather fiber composites[J].Polymer Composites,1998(4):431-439. |
| [12] | 胡雪敏,肖长发,封严.胶原蛋白改性聚丙烯腈纤维制备及性能表征[J].功能材料,2013(10):1414-1417. |
| [13] | Madera-Santana T J;Aguilar-Vega M J;Marquez A et al.Production of leather-like composites using short leather fibers Ⅱ.Mechanical characterization[J].Poly-mer Composites,2002,23(6):991-1002. |
| [14] | Su R X;Liu L L;Cui X L M M.Study on synthe-sis and application of collagen-modified polylactic acid[J].Polymer Composites,2014 |
| [15] | 杨奎,汪建根,张新强.有机硅丙烯酸酯双改性明胶皮革涂饰剂的研制[J].西部皮革,2007(06):18-21,29. |
| [16] | 张慧洁,丁志文,庞晓燕,程宝箴.水解胶原蛋白及其表征的研究进展[J].皮革与化工,2013(01):17-21,29. |
| [17] | Zhang X Y;Wang H R .Preparations of gelatins form leather waste and its application in leather[J].Environ-mental Engineering,2009,27(S1):346-348. |
| [18] | Su D Q;Wang K Y;Chen X W et al.Graft polymeriza-tion of acrylic monomers and collagen hydrolyzate[J].China Leather,2009,38(5):21-26. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%