通过电化学噪声技术(EN)、动电位扫描法、噪声电阻(Rn)等方法研究了304L 不锈钢在含 Cl－溶液中的腐蚀行为过程,探讨了Cl－对304L不锈钢腐蚀行为的影响,以及腐蚀的形成、特征、机理。结果表明,由于有Cl－的存在,对不锈钢金属的钝化膜的破坏必然导致腐蚀过程中离子扩散速度的加快,因此,Cl－对304L不锈钢腐蚀行为有着明显的钝化作用。
The corrosion behavior of 304L stainless steel in the role of Cl- was investigated by electrochemical noise (EN),potentiodynamic method and wavelet transform,as well as noise resistance (Rn).To investigate the effect of Cl- on the corrosion of stainless steel,as well as the formation of corrosion,characteristics,mech-anism.It was revealed that due to the presence of Cl-,damage to the stainless steel metal passivation film inev-itably lead to accelerate ion diffusion rate in the corrosion process,Cl- on the corrosion behavior of 304L stain-less steel passivation has a significant role.
参考文献
| [1] | Aballe A;Bethencourt M;Botana F J et al.Using wave-let transform in the analysis of electrochemical noise data[J].Electrochimica Acta,1999,44:4805-4816. |
| [2] | 李超群,李新海,王志兴,郭华军.镀镍冲孔钢带的耐蚀性能和电化学机理研究[J].功能材料,2014(03):03042-03046. |
| [3] | Cao Chunman.Principles of electrochemistry of corrosion[M].北京:化学工业出版社,2004:295-297. |
| [4] | Muniandy S V;Chew W X;Kan C S .Multifractal model-ing of electrochemical noise in corrosion of carbon steel[J].Corrosion Science,2011,53:188-200. |
| [5] | Cheng Y;Luo J;Wilmot M .Spectral analysis of electro-chemical noise with different transient shapes[J].Elec-trochim Acta,2000,45:1763. |
| [6] | Lafron A;Zhang T W;Jin S et al.Pitting corrosion of AZ91D and AJ62x magnesium alloys in alkaline chloride medium using electrochemical techniques[J].Electro-chim Acta,2005,51:489. |
| [7] | Li Ji;Zhao Lin;Li Bowen et al.Electrochemical noise a-nalysis of 304 stainless steel pitting corrosion in ferric chlorids solution[J].Journal of Chinese Society for Corro-sion and Protection,2012,32:236-242. |
| [8] | 刘栓,孙虎元,孙立娟.pH值和温度对镀锌钢在模拟锈层溶液中电化学腐蚀行为的影响[J].功能材料,2013(06):858-861,865. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%