将异佛尔酮二异氰酸酯(IPDI)加到端羟基聚二甲基硅氧烷(PDMS)和聚乙二醇(PEG600)混合物中进行反应，生成端基为异氰酸酯基的聚氨酯预聚体，用二羟甲基丙酸(DMPA)进行亲水扩链，季戊四醇三丙烯酸酯(PETA)引入光固化基团，然后用三乙胺中和，最后加水乳化，合成了一种有机硅改性水性聚氨酯乳液(WPUA-Si)。通过 FT-IR、TG、吸水率测试对其进行了研究。结果表明，有机硅改性的水性聚氨酯树脂的耐水性和热稳定性均有所提高。采用实时(real time)红外光谱原位(in situ)跟踪监测了该树脂的光固化动力学行为，结果表明，当光引发剂 Darocur1173含量为树脂质量的5％(质量分数)，体系光固化速率为最优。此外，增大辐照光强也有利于树脂的光固化。
The PUA prepolymer with isocyanate ending group has been prepared by the addition of isophorone diisocyanate (IPDI)with the mixture of polyethylene glycol (PEG600)and hydroxyl-ending polydimethylsilox-ane (PDMS).And then using dimethlolpropionic acid (DMPA)as a hydrophilic,pentaerythritol triacrylate (PETA)as an UV-curing groups and triethylamine (TEA)as a neutralizer,the waterborne polyurethane modi-fied with organosilicone (WPUA-Si)was eventually obtained through the emulsification.The structure and property of the WPUA-Si oligomer was characterized using infrared spectroscopy (FT-IR)and TG.The results show that water resistance and thermal stability of the UV-cured film of the WPUA-Si oligomer was improved. The UV-curing kinetics of the WPUA-Si oligomer was also investigated by real time FT-IR.When the amount of photoinitiator Darocur1 173 was 5wt%,UV-curing rate of the WPUA-Si oligomer was quickly and the conver-sion of the double bond was higher up to 90%.The light intensity of the radiation increasing can improve the UV-curing rate of the system.
参考文献
| [1] | Yang J W;Zeng Z H;Chen Y L.UV-curable coat-ings and application[M].北京:化学工业出版社,2011:11. |
| [2] | Yao Y P;Cui Y Y;Liu X X et al.The research progress of waterborne UV curing coating[J].Paint & Coating In-dustry,2011,41(08):74-76. |
| [3] | Yang, ZL;Wicks, DA;Hoyle, CE;Pu, HT;Yuan, JJ;Wan, DC;Liu, YS .Newly UV-curable polyurethane coatings prepared by multifunctional thiol- and ene-terminated polyurethane aqueous dispersions mixtures: Preparation and characterization[J].Polymer: The International Journal for the Science and Technology of Polymers,2009(7):1717-1722. |
| [4] | 陈子栋,张胜文,郭盟,刘秋华,刘晓亚.聚硅氧烷改性光固化水性聚氨酯的制备与性能研究[J].涂料技术与文摘,2013(12):22-26. |
| [5] | Zhang, T;Wu, WJ;Wang, XJ;Mu, YP .Effect of average functionality on properties of UV-curable waterborne polyurethane-acrylate[J].Progress in Organic Coatings: An International Review Journal,2010(3):201-207. |
| [6] | Z.H. Fang;H.Y. Duan;Z.H. Zhang;J. Wang;D.Q. Li;Y.X. Huang;J.J. Shang;Z.Y. Liu .Novel heat-resistance UV curable waterborne polyurethane coatings modified by melamine[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2011(11):4765-4768. |
| [7] | 邓朝霞,叶代勇,黄洪,陈焕钦.环氧树脂改性水性聚氨酯的合成研究[J].功能材料,2007(07):1132-1135. |
| [8] | 全一武,陈庆民,余学海.含聚二甲基硅氧烷聚氨酯（脲）的研究进展[J].高分子材料科学与工程,2003(06):1-5. |
| [9] | Emel Yilgor;Iskender Yilgor .Silicone containing copolymers: Synthesis, properties and applications[J].Progress in Polymer Science,2014(6):1165-1195. |
| [10] | Huang S Q;Sun Z G;Li S B.New organic silicon polymer material[M].北京:化学工业出版社,2004:14-16. |
| [11] | Yang JM.;Lin HT.;Lai WC. .Properties of modified hydroxyl-terminated polybutadiene based polyurethane membrane[J].Journal of Membrane Science,2002(1/2):105-117. |
| [12] | Jiang X S;Xu H J;Yin J et al.Polymeric amine bear-ing side-chain thioxanthone as a novel photoinitiator for photopolymerization[J].POLYMER,2004,45(01):133-140. |
| [13] | Pan Z R.Polymer chemistry[M].Beijing:Chemical In-dustry Press,2007:74. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%