将单宁酸(TA)改性的凹凸棒土(ATP)与聚偏氟乙烯(PVDF)和致孔剂聚乙二醇(PEG)混合,通过浸没沉淀相转化法制备了 PVDF/TA-ATP 杂化膜。利用差示扫描量热仪(DSC)和扫描电子显微镜(SEM)对杂化膜的热性能及微观形貌进行了表征,采用热力学相图和超声反射方法探讨了凝固浴组成对膜成膜过程的影响,进而研究了凝固浴组成对膜水通量的影响。研究结果表明,随着凝固浴中乙醇、N,N-二甲基甲酰胺(DMF)含量的增加,PVDF/TA-ATP 体系耐非溶剂能力增强,成膜速度减慢,膜孔结构由指状孔向海绵层结构渐变,纯水通量整体呈增大趋势。
In this work,attapulgite modified by tannic acid (TA),PVDF and porogen polyethylene glycol (PEG)were mixed and PVDF/TA-ATP flat sheet hybrid membrane was prepared by the method of phase in-version.The thermal properties and morphology of the hybrid membrane was characterized by differential scan-ning calorimetry and scanning electron microscopy,respectively.The effect of coagulation bath composition on the hybrid membrane in membrane-forming progress and then the pure water flux were studied by the method of thermodynamic phase diagram and ultrasonic reflection.The results showed that by adding more ethanol and DMF to the coagulation bath,more non-solvent was needed for phase separation,and the membrane-forming speed slowed significantly,the pore structure changed from finger-like pores with density skin into sponge-like pores without skin,the pure water flux increased.
参考文献
| [1] | Wang LH.;Sheng J. .Graft polymerization and characterization of butyl acrylate onto silane-modified attapulgite[J].Journal of Macromolecular Science. Pure and Applied Chemistry,2003(11):1135-1146. |
| [2] | Fan QH;Shao DD;Hu J;Wu WS;Wang XK .Comparison of Ni2+ sorption to bare and ACT-graft attapulgites: Effect of pH, temperature and foreign ions[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,2008(3):778-785. |
| [3] | 张亮亮,汪咏梅,徐曼,吴冬梅,陈笳鸿.植物单宁化学结构分析方法研究进展[J].林产化学与工业,2012(03):107-116. |
| [4] | Xia Sun;Xin Huang;Xue-pin Liao;Bi Shi .Adsorptive removal of Cu(Ⅱ) from aqueous solutions using collagen-tannin resin[J].Journal of hazardous materials,2011(2/3):1058-1063. |
| [5] | 李战胜,李恕广,江成璋.浸入凝胶法聚合物膜形成机理的研究现状[J].膜科学与技术,2002(02):29-36. |
| [6] | I.M. Wienk;R.M Boom;M.A.M. Beerlage;A.M.W. Bulte;C.A. Smolders;H. Strathmann .Recent advances in the formation of phase inversion membranes made from amorphous or semi-crystalline polymers[J].Journal of Membrane Science,1996(2):361-371. |
| [7] | Mulder M.Basic principles of membrane technology(sec-ond edition)[M].北京:清华大学出版社,1997 |
| [8] | Liu X T;Zhang G F;Zhao Y P et al.Preparation and adsorption of Ni(Ⅱ)of PVDF/modified attapulgite com-posite menbrane[J].Journal of Functional Materials,2013,44(24):3546-3549. |
| [9] | Qin J J;Jiang C Z .The investigation of phase diagrams of polysulfone membrane forming system[J].Membrane Science and Technology,1990,10(03):13-18. |
| [10] | Feng X;Guo Y F;Chen X et al.Membrane formation process and mechanism of PVDF-g-PNIPAAm thermo-sensitive membrane[J].DESALINATION,2012,290:89-98. |
| [11] | Yiping Zhao;Jingna Bai;Xia Feng;Li Chen;Xiang Shen;Meijun Liu;Jianxin Li .Properties of poly(vinylidene fluoride)-graft-poly (N-isopropylacrylamide) membranes prepared by alkali treatment[J].Journal of Polymer Research,2013(2):32-1-32-8. |
| [12] | 冯霞,郭艳芬,赵义平,李建新,陈熙,贺晓凌,陈莉.凝固浴温度对PVDF-g-PNIPAAm温度敏感膜成膜过程与性能的影响[J].高等学校化学学报,2011(06):1424-1430. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%