通过加速腐蚀实验研究4种氧化铁皮组织对热轧带钢腐蚀性能的影响.实验结果表明,经过80周期的加速腐蚀后,组织由Fe3O4和FeO构成的氧化铁皮最耐腐蚀.组织由Fe3O4、共析产物(Fe3O4+Fe)构成的氧化铁皮耐腐蚀性能最差.在腐蚀初期,腐蚀产物在氧化铁皮表面的缺陷处优先形核,随后外锈层形成.随着外锈层逐渐长大,在氧化铁皮缺陷处形成的腐蚀产物的体积变大.氧化铁皮缺陷处会形成裂纹并扩展到基体,形成内锈层的腐蚀核.在腐蚀后期,外锈层厚度继续长大,结合面处的腐蚀核长大形成内锈层,这时氧化铁皮失去保护作用.
参考文献
[1] | A. Collazo;X. R. Novoa;C. Perez;B. Puga.EIS study of the rust converter effectiveness under different conditions[J].Electrochimica Acta,200825(25):7565-7574. |
[2] | F.J. Perez;L. Martinez;M.P. Hierro;C. Gomez;A.L. Portela;G.N. Pucci;D. Duday;J. Lecomte-Beckers;Y. Greday.Corrosion behaviour of different hot rolled steels[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,20062(2):472-480. |
[3] | Jan Macak;Petr Sajdl;Pavel Kucera;Radek Novotny;Jan Vosta.In situ electrochemical impedance and noise measurements of corroding stainless steel in high temperature water[J].Electrochimica Acta,200617(17):3566-3577. |
[4] | Vourlias, G;Pistofidis, N;Chrissafis, K.High-temperature oxidation of precipitation hardening steel[J].Thermochimica Acta,20081/2(1/2):28-33. |
[5] | F. Velasco;A. Bautista;A. Gonzalez-Centeno.High-temperature Oxidation And Aqueous Corrosion Performance Of Ferritic, Vacuum-sintered Stainless Steels Prealloyed With Si[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,20091(1):21-27. |
[6] | C. F. Dong;H. B. Xue;X. G. Li;H. B. Qi;Y. F. Cheng.Electrochemical corrosion behavior of hot-rolled steel under oxide scale in chloride solution[J].Electrochimica Acta,200917(17):4223-4228. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%