在固体酸催化下,以苯基三乙氧基硅烷(PTES)、二甲基二乙氧基硅烷(DMES)、四甲基环四硅氧烷(D4 H )、八甲基环四硅氧烷(D4)、六甲基二硅氧烷(MM)和四甲基二硅氧烷(D2 H )为主要原料,通过水解缩聚法合成了一系列Si—H 键、D链节含量分别不同的含氢苯基硅树脂 HPSR.用傅里叶变换红外光谱(FT-IR)和核磁共振氢谱(1 H NMR)对其进行了结构表征.将所制的 HPSR与乙烯基硅橡胶VPS以n(Si—H)∶n(Vi)＝1．2∶1．3的摩尔比混合,并加入剂量的络合铂催化剂、铂抑制剂,以及占总质量10％的白炭黑和钛白粉,在160℃下固化10~15 min即制得透明的耐高温硅橡胶涂层,并对其耐热性和力学性能进行研究.结果表明,当 HPSR 分子中Si—H 键含量为5 mmol/g,MD∶MR＝10％时,对应制备的涂层耐热性、柔韧性以及力学性能最佳.
The hydrogen containing phenyl silicone resin (HPSR)was synthesized with hydrolysis-polyconden-sation method from phenyltriethoxysilane (PTES),methyltriethoxysilane (MTES),teteamethylcyclotetrasi-loxane (D4 H ),octamethylcyclotetrasioxane (D4 ),hexamethyldisiloxane (MM)and teteamethyldisiloane (D2 H ) in the presence of solid acid catalyst,which has different content of Si—H and D chain respectively.The struc-ture of the polymer was characterized through FT-IR and 1 H NMR.The HPSR and vinyl silicone rubber (VPS) was mixed with the molar ratio of n(Si—H)∶n(Vi)=1.2∶1.3,together with the dose of Pt catalyst,Pt inhib-itor,and 10% of silica and titanium dioxide,the high temperature silicone rubber coating was successively pre-pared with 160 ℃ sustained 10-15 min,and the high temperature and mechanical properties were also studied. the results showed that when content of HPSR Si—H was 5 mmol/g,MD∶MR=10%,high resistance,flexi-bility and mechanical properties of the coating were the best.
参考文献
| [1] | 徐清钢;姚金水;李梅;马慧荣.耐高温有机硅树脂的合成和改性研究状况[J].山东轻工业学院学报（自然科学版）,2010(1):33-36. |
| [2] | 王宏刚;毛绍兰;高金堂.耐热有机硅树脂研究进展[J].粘接,2000(3):29-33. |
| [3] | Jovanovic JD.;Dvornic PR.;Popovic IG.;Govedarica MN..The thermogravimetric analysis of some polysiloxanes[J].Polymer Degradation and Stability,19981(1):87-93. |
| [4] | Yang, Z.;Han, S.;Zhang, R.;Feng, S.;Zhang, C.;Zhang, S..Effects of silphenylene units on the thermal stability of silicone resins[J].Polymer Degradation and Stability,201112(12):2145-2151. |
| [5] | 赵维;齐暑华;郭锦歌.耐高温硅树脂的合成[J].有机硅材料,2008(5):273-276. |
| [6] | 殷树梅;王志浩;孙红岩.有机硅涂料的研究及应用进展[J].有机硅材料,2011(6):414-417. |
| [7] | 明耀强;胡剑峰;张宇帆;黎永津;瞿金清.有机硅树脂耐高温改性研究进展[J].广东化工,2014(24):49-50,40. |
| [8] | 孙举涛;黄玉东;曹海琳;巩桂芬.耐高温有机硅树脂的合成及其耐热和固化性能研究[J].航空材料学报,2005(1):25-29,35. |
| [9] | 方炜敏;陈循军;冯凯琪;魏戈;邓思韵;程杏.苯基含氢硅树脂的制备及固化性能研究[J].仲恺农业工程学院学报,2014(3):14-17,28. |
| [10] | 贾梦秋;邓海锋.耐高温有机硅树脂的合成[J].化工新型材料,2007(7):46-48. |
| [11] | Dongzhi Chen;Shengping Yi;Pengfei Fang;Yalan Zhong;Chi Huang;Xiaojun Wu.Synthesis and characterization of novel room temperature vulcanized (RTV) silicone rubbers using octa [(trimethoxysilyl)ethyl]-POSS as cross-linker[J].Reactive & functional polymers,20114(4):502-511. |
| [12] | 徐镇田;沈星星;周魏华;陈义旺.LED封装用乙烯基硅油的制备与固化性能[J].化工新型材料,2010(5):109-111. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%