采用单质Mn、Cu、Ni、Fe粉末,通过反应烧结过程可制备 M2052合金.主要研究了烧结温度对密度、孔隙率和力学性能的影响,同时对烧结样品的相组成进行了分析.M2052合金在950℃烧结时基本为γ-MnCu固溶体,合金的密度为6．23 g/cm3,致密度为87．2％,抗弯强度达到了487 MPa,并具有良好的阻尼性能,不同频率下的阻尼性能表现稳定,损耗因子tanδ达到0．11~0．12.
M2052 damping alloy was prepared through reaction sintered method using high-purity simple sub-stance powders of Mn、Cu、Ni、Fe.Not only the effect of different sintering temperature on the density,porosity and mechanical properties of the sintering alloy was studied,but also the phase composition of the sintered sam-ple was analyzed.It is demonstrated that the M2052 alloy sintered at 1 223 K was essentiallyγ-MnCu solid solu-tion.The density of M2052 alloy sintered at 1 223 K was 6.23 g/cm-3 ,the relative density was 87.2% and the bending strength reach to 487 MPa.The results show that the damping capacity maintained at a very high level (tanδranges from 0.11-0.12)and the damping ability changes little as frequency increases from 0-100 Hz.
参考文献
| [1] | Y. Q. Wu;F. X. Yin;K. Hono.The decomposed γ-phase microstructure in a Mn-Cu-Ni-Fe alloy studied by HRTEM and 3D atom probe[J].Scripta materialia,200210(10):717-722. |
| [2] | 于学勇;郭国林;杨莉.Fe-Mn基高阻尼合金的研究现状及展望[J].铸造技术,2012(7):774-776. |
| [3] | 刘广;张振忠;张少明;沈晓冬;马立群.高阻尼镁锆合金的研究进展及展望[J].材料导报,2006(z2):425-428,439. |
| [4] | 李沛勇;戴圣龙;刘大博;柴世昌;李裕仁.材料阻尼及阻尼合金的研究现状[J].材料工程,1999(8):44-48. |
| [5] | 王敬丰;魏文文;潘复生;汤爱涛;丁培道.金属阻尼材料研究的新进展及发展方向[J].材料导报,2009(13):15-19. |
| [6] | 宋玉强;李世春.铜与锰金属粉末的烧结特性[J].石油大学学报(自然科学版),2001(5):76-78. |
| [7] | 邓华铭;张骥华;陈树川.γMn－Cu合金在（γ＋α）亚稳互溶区时效过程Spinodal分解的热力学判据[J].功能材料与器件学报,2001(1):69-72. |
| [8] | I.S. Golovin;H.-R. Sinning;I.K. Arhipov.Damping in some cellular metalic materials due to microplasticity[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20041/2(1/2):531-536. |
| [9] | M. Fukuhara;F. Yin;Y. Ohsawa.High-damping properties of Mn-Cu sintered alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20061/2(1/2):439-443. |
| [10] | Y. Zhong;F. Yin;T. Sakaguchi.Dislocation structure evolution and characterization in the compression deformed Mn-Cu alloy[J].Acta materialia,20078(8):2747-2756. |
| [11] | 张新建;朱博洪;牛德良;杨剑;徐敏人;肖扬武.Al2O3/SiO2对烧结矿冶金性能的影响[J].重庆理工大学学报（自然科学版）,2014(2):40-44. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%