利用XRD、Raman、FT-IR、TEM、循环伏安、恒流充放电、交流阻抗等方法研究了微波法制备的石墨烯包覆硅材料(Si/RGO)的结构、形貌及其电化学性能.XRD、Raman、FT-IR 结果表明,微波加热能够将氧化石墨烯还原为石墨化程度较低且无序度增加的石墨烯；TEM显示石墨烯均匀包覆着纳米硅,包覆厚度大约为4 nm；充放电结果表明,石墨烯包覆硅材料具有较高的可逆比容量、良好的倍率性能和较好的循环稳定性,在400 mA/g电流密度下,首次脱锂比容量为1747 mAh/g,库伦效率为67．4％,经3次循环之后,每一循环电量转换效率均在98％以上,循环100周后,可逆的嵌脱锂比容量仍可达1175 mAh/g.
The graphene coated silicon composite (Si/RGO)was synthesized by microwave method.The struc-ture,morphology and electrochemical performances of the as-prepared samples were studied by methods of XRD,Raman,FT-IR,TEM,cyclic voltammetry,galvanostatic charge-discharge and AC impedance.The XRD,Raman and FT-IR results showed that graphene oxide was reduced tographenewith low graphitization de-gree and disordered increased.The TEM images indicated that the nano silicon was evenly coated with gra-phene,with thickness of about 4 nm.Charge and discharge results show that graphene coated silicon samples showed high specific capacity,goodrate performance and cycle stability.The initial discharge specific capacity and the coulomb efficiency was 1 747 mAh/g and 67.4%.The power conversion efficiency was increased to 98%after 3 cycles at a current density of 400 mA/g.After 100 cycles at 400 mA/g,the reversible specific capacity retained 1 1 7 5 mAh/g.
参考文献
| [1] | Mori, Tatsuhiro;Chen, Chih-Jung;Hung, Tai-Feng;Mohamed, Saad Gomaa;Lin, Yi-Qiao;Lin, Hong-Zheng;Sung, James C.;Hu, Shu-Fen;Liu, Ru-Shi.High specific capacity retention of graphene/silicon nanosized sandwich structure fabricated by continuous electron beam evaporation as anode for lithium-ion batteries[J].Electrochimica Acta,2015:166-172. |
| [2] | Yue, Hongwei;Wang, Suiyan;Yang, Zhibo;Li, Qun;Lin, Shumei;He, Deyan.Ultra-thick porous films of graphene-encapsulated silicon nanoparticles as flexible anodes for lithium ion batteries[J].Electrochimica Acta,2015:688-695. |
| [3] | Zhang, Fan;Yang, Xi;Xie, Yuqing;Yi, Ningbo;Huang, Yi;Chen, Yongsheng.Pyrolytic carbon-coated Si nanoparticles on elastic graphene framework as anode materials for high-performance lithium-ion batteries[J].Carbon: An International Journal Sponsored by the American Carbon Society,2015:161-167. |
| [4] | Tang, H.;Zhang, J.;Zhang, Y. J.;Xiong, Q. Q.;Tong, Y. Y.;Li, Y.;Wang, X. L.;Gu, C. D.;Tu, J. P..Porous reduced graphene oxide sheet wrapped silicon composite fabricated by steam etching for lithium-ion battery application[J].Journal of Power Sources,2015Jul.15(Jul.15):431-437. |
| [5] | 徐宇虹 .锂离子电池硅负极的失效行为与性能改进[D].哈尔滨工业大学,2010. |
| [6] | Wei Chen;Nan Jiang;Zhongli Fan;Abirami Dhanabalan;Chunhui Chen;Yunjun Li;Mohshi Yang;Chunlei Wang.Facile synthesis of silicon films by photosintering as anode materials for lithium-ion batteries[J].Journal of Power Sources,2012Sep.15(Sep.15):21-27. |
| [7] | Alireza Kohandehghan;Peter Kalisvaart;Kai Cui.Silicon nanowire lithium-ion battery anodes with ALD deposited TiN coatings demonstrate a major improvement in cycling performance[J].Journal of Materials Chemistry, A. Materials for energy and sustainability,201341(41):12850-12861. |
| [8] | Osafo-Acquaah, A;Foster, DG;Jorne, J.Isotropic effect of fluid flow on scaling of surface roughness during copper electrodeposition[J].Journal of the Electrochemical Society,20084(4):D270-D277. |
| [9] | Wu, Junxiong;Qin, Xianying;Zhang, Haoran;He, Yan-Bing;Li, Baohua;Ke, Lei;Lv, Wei;Du, Hongda;Yang, Quan-Hong;Kang, Feiyu.Multilayered silicon embedded porous carbon/graphene hybrid film as a high performance anode[J].Carbon: An International Journal Sponsored by the American Carbon Society,2015:434-443. |
| [10] | Congxiang Lu;Yu Fan;Hong Li.Gore-shell CNT-Ni-Si nanowires as a high performance anode material for lithium ion batteries[J].Carbon: An International Journal Sponsored by the American Carbon Society,2013:54-60. |
| [11] | Min Zhou;Fan Pu;Zhao Wang.Facile synthesis of novel Si nanoparticles-graphene composites as high-performance anode materials for Li-ion batteries[J].Physical chemistry chemical physics: PCCP,201327(27):11394-11401. |
| [12] | Hai Li;Chunxiang Lu;Baoping Zhang.A straightforward approach towards Si@C/graphene nanocomposite and its superior lithium storage performance[J].Electrochimica Acta,2014:96-101. |
| [13] | Becerril, H.A.;Mao, J.;Liu, Z.;Stoltenberg, R.M.;Bao, Z.;Chen, Y..Evaluation of solution-processed reduced graphene oxide films as transparent conductors[J].ACS nano,20083(3):463-470. |
| [14] | Yong-Sheng Hu;Rezan Demir-Cakan;Maria-Magdalena Titirici.Superior Storage Performance of a Si@SiO_x/C Nanocomposite as Anode Material for Lithium-Ion Batteries[J].Angewandte Chemie,20089(9):1645-1649. |
| [15] | Lei Gan;Huajun Guo;Zhixing Wang;Xinhai Li;Wenjie Peng;Jiexi Wang;Silin Huang;Mingru Su.A facile synthesis of graphite/silicon/graphene spherical composite anode for lithium-ion batteries[J].Electrochimica Acta,2013:117-123. |
| [16] | Xingfa Gao;Joonkyung Jang;Shigeru Nagase.Hydrazine and Thermal Reduction of Graphene Oxide: Reaction Mechanisms, Product Structures, and Reaction Design[J].The journal of physical chemistry, C. Nanomaterials and interfaces,20102(2):832-842. |
| [17] | Tang, H.;Zhang, Y. J.;Xiong, Q. Q.;Cheng, J. D.;Zhang, Q.;Wang, X. L.;Gu, C. D.;Tu, J. P..Self-assembly silicon/porous reduced graphene oxide composite film as a binder-free and flexible anode for lithium-ion batteries[J].Electrochimica Acta,2015:86-93. |
| [18] | Yu Liu;Yulong Ying;Yiyin Mao.CuO nanosheets/rGO hybrid lamellar films with enhanced capacitance[J].Nanoscale,201319(19):9134-9140. |
| [19] | Shah, Sayyar Ali;Cui, Lan;Lin, Kui;Xue, Tao;Guo, Qianjin;Li, Ling;Zhang, Lishuang;Zhang, Fan;Hu, Fengxiang;Wang, Xitao;Wang, Hui;Chen, Xiaoping;Cui, Shen.Preparation of novel silicon/nitrogen-doped graphene composite nanosheets by DC arc discharge[J].RSC Advances,201537(37):29230-29237. |
| [20] | J.C. Meyer;A.K. Geim;M.I. Katsnelson;K.S. Novoselov;D. Obergfell;S. Roth;C. Girit;A. Zettl.On the roughness of single- and bi-layer graphene membranes[J].Solid State Communications,20071/2(1/2):101-109. |
| [21] | Xue, L.;Fu, K.;Li, Y.;Xu, G.;Lu, Y.;Zhang, S.;Toprakci, O.;Zhang, X..Si/C composite nanofibers with stable electric conductive network for use as durable lithium-ion battery anode[J].Nano Energy,20133(3):361-367. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%