采用自主开发的无氟化学溶液沉积法在(00l)LaAlO3单晶片上制备了 SmBa2 Cu3 O7－x (SmBCO)超导薄膜,研究了涂层溶液的粘度对SmBCO 超导薄膜织构、微结构及超导性能的影响.通过调节前驱溶液中高分子的添加量来调控涂层溶液的粘度.结果表明,不同高分子添加量的涂层溶液制备的薄膜均具有较好的c 轴单晶取向,其中高分子添加量为4％的涂层溶液制备的超导薄膜表面更加平整、致密,显示了良好的晶粒连接性.此外,该粘度的涂层溶液制备的薄膜超导转变温度为89．5 K,临界电流密度(65 K,自场)达到1 MA/cm2以上,显示了较好的超导电性.
SmBCO superconducting films were deposited on (00l)LaAlO3 single crystal substrate by self-devel-oped fluorine-free chemical solution deposition approach.The effect of the solution viscosity on the texture,mi-crostructure and superconducting properties of the films were investigated.In this work,the solution viscosity was adj usted by changing the amount of polymers in the precursor solution.The results indicate that SmBCO films with different viscosities show good c-axis texture of the grains.And the film with 4% polymer addition in the precursor solution has much smoother and denser surface morphologies,showing the good grains connectiv-ity.In addition,this film has a high TC of 89.5 K and J c(65 K,self-field)above 1 MA/cm2 ,illustrating better superconductivity.
参考文献
| [1] | 雷黎;赵高扬;徐慧.Zn^2＋掺杂的YBCO薄膜的超导性能研究[J].功能材料,2011(11):2116-2118. |
| [2] | Cardwell DA;Babu NH.Processing and properties of single grain (RE)-Ba-Cu-O bulk superconductors[J].Physica, C. Superconductivity and its applications,20060(0):1-7. |
| [3] | R. Fuger;M. Eisterer;S.S. Oh;H.W. Weber.Superior properties of SmBCO coated conductors at high magnetic fields and elevated temperatures[J].Physica, C. Superconductivity and its applications,20105/6(5/6):323-325. |
| [4] | Iguchi T.;Araki T.;Yamada Y.;Ikuta H.;Hirabayashi I.;Shiohara Y. Mizutani U..Metal-organic deposition of RE-Ba-Cu-O (RE = Dy, Ho, Er, and Tm) films using trifluoro acetates[J].Physica, C. Superconductivity and its applications,2003Pt.2(Pt.2):900-904. |
| [5] | Wang, WT;Li, G;Pu, MH;Sun, RP;Zhou, HM;Zhang, Y;Zhang, H;Yang, Y;Cheng, CH;Zhao, Y.Chemical solution deposition of YBCO thin film by different polymer additives[J].Physica. C, Superconductivity and its applications,200815/20(15/20):1563-1566. |
| [6] | W.T. Wang;Y. Zhao;M.H. Pu.High performance fluorine-free MOD YBa_2Cu_3O_(7-z) film preparation by partial melting process[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2012:610-614. |
| [7] | S. Morlens;N. Roma;S. Ricart.Thickness control of solution deposited YBCO superconducting films by use of organic polymeric additives[J].Journal of Materials Research,20078(8):2330-2338. |
| [8] | Q. X. Jia;T. M. Mccleskey;A. K. Burrell;Y. Lin;G. E. Collis;H. Wang;A. D. Q. Li;S. R. Foltyn.Polymer-assisted deposition of metal-oxide films[J].Nature materials,20048(8):529-532. |
| [9] | Y. Lin;Jang-Sik Lee;H. Wang;Y. Li;S. R. Foltyn;Q. X. Jia;G. E. Collis;A. K. Burrell;T. M. McCleskey.Structural and dielectric properties of epitaxial Ba_(1-x)Sr_(x)TiO_(3) films grown on LaAlO_(3) substrates by polymer-assisted deposition[J].Applied physics letters,200421(21):5007-5009. |
| [10] | M. Jain;Y. Li;M. F. Hundley;M. Hawley;B. Maiorov;I. H. Campbell;L. Civale;Q. X. Jia;P. Shukla;A. K. Burrell;T. M. McCleskey.Magnetoresistance in polymer-assisted deposited Sr- and Ca-doped lanthanum manganite films[J].Applied physics letters,200623(23):232510-1-232510-3-0. |
| [11] | Kawashima J.;Hirabayashi I.;Yamada Y..Critical thickness and effective thermal expansion coefficient of YBCO crystalline film[J].Physica, C. Superconductivity and its applications,19981/2(1/2):114-118. |
| [12] | Foltyn SR;Wang H;Civale L;Jia QX;Arendt PN;Maiorov B;Li Y;Maley MP;MacManus-Driscoll JL.Overcoming the barrier to 1000 A/cm width superconducting coatings[J].Applied physics letters,200516(16):2505-1-2505-3-0. |
| [13] | B. W. Kang;A. Goyal;D. F. Lee.Comparative study of thickness dependence of critical current density of YBa_2Cu_3O_(7-delta) on (100) SrTiO_3 and on rolling-assisted biaxially textured substrates[J].Journal of Materials Research,20027(7):1750-1757. |
| [14] | Guoxing Li;Shanwen Li;Wei Li;Xinsheng Wang;Feng Guo;Baolin Zhang;PenChu Chou.Higher oxidization rate of photo-assisted annealing compared with thermal annealing after YBa_2Cu_3O_(7-δ) films growth[J].Physica, C. Superconductivity and its applications,2014:17-21. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%