为了探究疲劳加载对橡胶钢丝复合体粘合性能的影响，采用动态测量与静态测量相结合的办法，研究疲劳频率、疲劳加载次数和动态疲劳后停放时间对橡胶钢丝复合体粘合性能的影响，结果表明，随着疲劳频率的逐渐提高，试样断裂时拉伸伸长量表现出明显降低的趋势；橡胶钢丝复合体试样抽出粘合力和钢丝帘线的表面附胶量均随着疲劳次数的增加先增大后减小；同样，粘合力随着停放时间的延长也是先增大后减小，并且橡胶钢丝复合体疲劳后粘合力的恢复主要发生在停放初期。
In order to explore the influence of fatigue loading on the adhesive properties of rubber-steel wire com-plexes.In this paper,dynamic and static measurement methods are integrated using to research the influence of these items on the adhesive properties of rubber-steel wire complexes,which items contain fatigue frequency,fa-tigue loading times and storage time after dynamic fatigue measurement.The results show that the tensile elon-gation of sample at fracture shows obviously decreased with the increasing of fatigue frequency.The extraction force of rubber-steel wire complexes sample shows a variation tendency of firstly increases and then decreases with the increase of fatigue imposed times.In addition,the steel cord surface adhesive amount shows a variation tendency of firstly increases and then decreases with the increase of fatigue imposed times.The adhesion force also has a variation tendency of firstly increases and then decreases with the increasing of storage time,and the recovery of adhesion force after fatigue imposed mainly occurred in the initial stage of storage time.
参考文献
| [1] | 马明强;赵鑫;史新妍.动态疲劳对钢丝帘线/橡胶粘合性能的影响[J].橡胶工业,2015(2):80-84. |
| [2] | 陈毅敏;张英.橡胶-帘线粘合性能在动态及加热条件下的评价方法[J].轮胎工业,2014(3):188-190. |
| [3] | 田振辉;谭惠丰;谢礼立.橡胶复合材料疲劳破坏特性[J].复合材料学报,2005(1):32-35. |
| [4] | Zhang P;Shi XY;Li J;Yu GS;Zhao SG.Effects of hot-air aging and dynamic fatigue on the structure and dynamic viscoelastic properties of unfilled natural rubber vulcanizates[J].Journal of Applied Polymer Science,20083(3):1911-1916. |
| [5] | 郑爱隔;马明强;李琦;史新妍.疲劳温度对橡胶与钢丝帘线动态粘合性能的影响[J].弹性体,2014(1):15-18,36. |
| [6] | Chandra AK.;Bhowmick AK.;Mukhopadhyay R..STUDIES OF DYNAMIC ADHESION BETWEEN STEEL CORD AND RUBBER USING A NEW TESTING METHOD[J].Polymer Testing,19961(1):13-34. |
| [7] | 胡嘉文;陈慧;张宏泽;李雪玉;王重.天然橡胶与镀铜钢丝帘线粘接机理的研究进展[J].弹性体,2015(1):85-90. |
| [8] | 刘宇艳;谭惠丰;万志敏;杜星文.单向帘线增强橡胶复合材料在疲劳过程中的温升[J].宇航材料工艺,1999(5):30-33. |
| [9] | Janssen RPM;Govaert LE;Meijer HEH.An analytical method to predict fatigue life of thermoplastics in uniaxial loading: Sensitivity to wave type, frequency, and stress amplitude[J].Macromolecules,20087(7):2531-2540. |
| [10] | DR. GUY BUYTAERT;FREDERIK COORNAERT;DR. WILLEM DEKEYSER.CHARACTERIZATION OF THE STEEL TIRE CORD — RUBBER INTERFACE[J].Rubber Chemistry and Technology,20094(4):430-441. |
| [11] | Mars WV;Fatemi A.Factors that affect the fatigue life of rubber: A literature survey[J].Rubber Chemistry and Technology,20043(3):391-412. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%