合成了 RAFT 试剂 S-1-十二烷基-S’-(α,α’-二甲基-α”-乙酸)三硫代碳酸酯(DDAATB),并以此种RAFT试剂为链转移剂制备聚丙烯酸均聚物,再以此均聚物为大分子链转移剂,制备了聚丙烯酸-b-聚丙烯酸异冰片酯嵌段共聚物(PAA-b-PIBOA)。以制备的丙烯酸酯嵌段共聚物作为附着力促进剂,与 UV 树脂复配成 UV涂料,考察了添加不同质量分数嵌段共聚物的涂料对PP基材的附着能力的改善,并与CPP进行了比较。研究结果表明,制备的丙烯酸酯嵌段共聚物可有效提高涂层对PP基材的粘附性,PIBOA链段分子量越大,效果越明显；将制备的 PAA-b-PIBOA 为附着力促进剂,分别添加至以聚酯丙烯酸酯、氯化聚醚为主体树脂的涂料配方中,通过附着力性能测试,发现合成的嵌段共聚物PAA-b-PIBOA能有效提高涂层对PP基材的附着力。
In this paper,a kind of RAFT agent named S-1-Dodecyl-S’-(a,a’-dimethyl-a”- acetic acid)-trithiocar-bonate (DDAATB)were synthesized.Polyacrylic acid is prepared by using the RAFT agent as a chain transfer agent,then use the polyacrylic acid as the macro-RAFT agent to prepare the block copolymer (PAA-b-PIBOA). Using this block copolymer as the adhesion promoter,it was added into the coatings formula with addition of different contents.Then the complex was separately painted to the PP substrate and cured.The peel strength of the coating was measured,and compared with CPP was made.The results showed that the prepared acrylate block copolymer can effectively improve the adhesion to the PP substrate.The greater the molecular weight of PIBOA segment,the more obviously of the adhesion effect.Meanwhile,PAA-b-PIBOA was added to the coat-ing formulation of polyester acrylate and chlorinated polyether resin,it could effectively be to improve the coat-ing adhesion on PP substrate.
参考文献
| [1] | Abdel-Hamid I. Mourad.Thermo-mechanical characteristics of thermally aged polyethylene/polypropylene blends[J].Materials & design,20102(2):918-929. |
| [2] | S.Mojtaba Mirabedini;Hamid Rahimi;Sh.Hamedifar;S.Mohsen Mohseni.Microwave irradiation of polypropylene surface:a study on wettability and adhesion[J].International Journal of Adhesion & Adhesives,20042(2):163-170. |
| [3] | Schellekens, M.;Twene, D.;Van Der Waals, A..Block copolymers for waterborne coatings-a novel eco-friendly approach for improved coating adhesion to untreated polypropylene based plastics[J].Progress in Organic Coatings: An International Review Journal,20111/2(1/2):138-143. |
| [4] | 赵兴顺;张军华;郑朝晖;潘毅;朱珠;丁小斌;彭宇行.溶液法马来酸酐接枝氯化聚丙烯的研究[J].功能高分子学报,2003(1):77-80. |
| [5] | 范忠雷;刘大壮;董雪茹;马向东.马来酸酐接枝率对氯化聚丙烯和醇酸树脂相容性的影响[J].塑料工业,2005(z1):168-170. |
| [6] | 马向东;刘大壮;孙培勤.氯化聚丙烯接枝马来酸酐的合成研究[J].涂料工业,2007(7):29-31. |
| [7] | 董雪茹;刘大壮;孙培勤;孙绍晖.丙烯酸改性氯化聚丙烯乳液[J].化工进展,2007(10):1449-1451,1474. |
| [8] | 董雪茹;刘大壮;孙培勤;孙绍晖.丙烯酸改性氯化聚丙烯乳液的合成与性能[J].涂料工业,2008(3):63-66. |
| [9] | 宋斌;李伟浩;李华亮;陆云;洪仰婉;何惠敏.氯化聚丙烯/丙烯酸酯接枝物的合成和性能研究[J].广东化工,2011(12):4-5. |
| [10] | 杨光欣;梁亮;赵立那.接枝共聚改性氯化聚丙烯乳液的研究[J].中国胶粘剂,2012(4):13-16. |
| [11] | 何佳杰;向贤伟.丙烯酸类单体接枝改性氯化聚丙烯乳液的制备[J].合成树脂及塑料,2012(5):43-46. |
| [12] | Yongping Bai;Chun Zhang;Minrui Li.Graft modification of chlorinated polypropylene and coating performance promotion for polypropylene[J].International Journal of Adhesion & Adhesives,2014:231-237. |
| [13] | 张柳;崔艳艳;刘晓暄.聚丙烯基材直涂无卤附着树脂概述[J].涂料工业,2015(3):81-86. |
| [14] | Yan Yan Cui;Ya E Ren;Xiao Xuan Liu.Synthesis of methyl methacrylate star-branched polymer with divinylbenzene as a linking agent via controlled/living photopolymerization[J].中国化学快报（英文版）,2012(08):985-988. |
| [15] | Ye, G.;Cui, Y.;Liu, X.;Zhou, H..Kinetic investigation of photopolymerization initiated by oligomeric photolatent base: Polymer effect or molecular amplification[J].Journal of thermal analysis and calorimetry,20133(3):1499-1506. |
| [16] | Liu, X.;Zhang, Y.;Cui, Y.;Dong, Z..Reactivity ratios and sequence structures of the copolymers prepared using photo-induced copolymerization of MMA with MTMP[J].Magnetic Resonance in Chemistry: MRC,20125(5):372-378. |
| [17] | Su, Jiahui;Liu, Xiaoxuan;Hu, Junqi;You, Qin;Cui, Yanyan;Chen, Yingyin.Photo-induced controlled radical polymerization of methyl methacrylate mediated by photosensitive nitroxides[J].Polymer international,20157(7):867-874. |
| [18] | 刘晓暄;张永涛;崔艳艳;杨伟胜;郭沛霏;董智贤.NIPAM共聚物多孔水凝胶的光引发RAFT合成及其溶胀性能[J].高分子学报,2011(6):672-678. |
| [19] | 赖俊伟;杨建文;刘晓暄.碳酸钙表面感光修饰及其在UV涂料中的应用[J].影像科学与光化学,2013(1):10-17. |
| [20] | 苏嘉辉;黄伟;杨雪娇;陈颖茵;罗青宏;刘晓暄.多官能度聚氨酯丙烯酸酯水性UV树脂的合成与性能表征[J].高分子材料科学与工程,2015(1):13-18. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%