采用高温固相法制备CrNbO4,并首次研究其作为锂离子电池负极材料的电化学性能.使用 X射线衍射分析(XRD)、扫描电子显微镜(SEM)、充放电测试、循环伏安(CV)测试和电化学交流阻抗测试(EIS)对材料的结构、形貌和电化学性能进行表征.样品 CrNbO4在0．001~3．0 V 电压区间,电流密度为16 mA/g 时,充放电50次后放电容量可以保持在63．5 mAh/g.通过球磨,CrNbO4的首次放/充电容量由212．9/100．9 mAh/g 提高到572．3/343．5 mAh/g,同时电流密度提高10倍,充放电50次后改性样品的放电容量仍可维持81．3 mAh/g,有效提高了电化学性能.
CrNbO4 was successively prepared by high solid-state method and first discussed its electrochemical properties as an anode material in lithium-ion batteries.The structure,morphology and electrochemical proper-ties were characterized using X-ray diffraction (XRD),scanning electron microscope (SEM),galvanostatic dis-charge-charge test,cyclic voltammetry (CV)and electrochemical impedance spectra (EIS).CrNbO4 can maintain a discharge capacity of 63.5 mAh/g after 50 cycles between 0.001-3.0 V at a current density of 16 mA/g.The initial dis-charge/charge capacity of sample improved from 212.9/100.9 mAh/g to 572.3/343.5 mAh/g through ball-milling meth-od,and discharge capacity kept 81.3 mAh/g after 50 cycles at a current density of 160 mA/g.
参考文献
| [1] | Yang, Z.;Zhang, J.;Kintner-Meyer, M.C.W.;Lu, X.;Choi, D.;Lemmon, J.P.;Liu, J..Electrochemical energy storage for green grid[J].Chemical Reviews,20115(5):3577-3613. |
| [2] | M. Armand;J.-M. Tarascon.Building better batteries[J].Nature,20087179(7179):652-657. |
| [3] | 刘宇;王保峰;解晶莹;杨军;陈健.二次锂电池中SEI膜的电化学性能表征[J].无机材料学报,2003(2):307-312. |
| [4] | A. J. Smith;J. C. Burns;Xuemei Zhao.A High Precision Coulometry Study of the SEI Growth in Li/Graphite Cells[J].Journal of the Electrochemical Society,20115(5):A447-A452. |
| [5] | Sundaramurthy Jayaraman;Vanchiappan Aravindan;Palaniswamy Suresh Kumar.Exceptional Performance of TiNb2O7 Anode in All One-Dimensional Architecture by Electrospinning[J].ACS applied materials & interfaces,201411(11):8660-8666. |
| [6] | Colin JF;Pralong V;Hervieu M;Caignaert V;Raveau B.Lithium insertion in an oriented nanoporous oxide with a tunnel structure: Ti2Nb2O9[J].Chemistry of Materials: A Publication of the American Chemistry Society,20084(4):1534-1540. |
| [7] | Jian-Tao Han;Yun-Hui Huang;John B. Goodenough.New Anode Framework for Rechargeable Lithium Batteries[J].Chemistry of Materials: A Publication of the American Chemistry Society,20118(8):2027-2029. |
| [8] | Jian-Tao Han;Dong-Qiang Liu;Sang-Hoon Song.Lithium Ion Intercalation Performance of Niobium Oxides: KNb5O_(13) and K6Nb_(10.8)O_(30)[J].Chemistry of Materials: A Publication of the American Chemistry Society,200920(20):4753-4755. |
| [9] | Reddy, MA;Pralong, V;Varadaraju, UV;Raveau, B.Crystallite size constraints on lithium insertion into brookite TiO2[J].Electrochemical and solid-state letters,20088(8):A132-A134. |
| [10] | Ji-Yong Shin;Dominik Samuelis;Joachim Maier.Sustained Lithium-Storage Performance of Hierarchical, Nanoporous Anatase TiO_2 at High Rates: Emphasis on Interfacial Storage Phenomena[J].Advanced functional materials,201118(18):3464-3472. |
| [11] | Guan-Nan Zhu;Yong-Gang Wang;Yong-Yao Xia.Ti-based compounds as anode materials for Li-ion batteries[J].Energy & environmental science: EES,20125(5):6652-6667. |
| [12] | Sato M.;Hama Y..LITHIUM INSERTION CHARACTERISTICS OF CUNB2O6[J].International Journal of Quantum Chemistry,19951(1):193-198. |
| [13] | M. Anji Reddy;U. V. Varadaraju.Lithium Insertion into Niobates with Columbite-Type Structure: Interplay between Structure-Composition and Crystallite Size[J].The journal of physical chemistry, C. Nanomaterials and interfaces,201150(50):25121-25124. |
| [14] | Samarasingha, Pushpaka B.;Thomas, Chris I.;Fjellvag, Helmer.Investigation of Li+ insertion in columbite structured FeNb2O6 and rutile structured CrNb2O6 materials[J].Electrochimica Acta,2015:232-237. |
| [15] | Jian, Z.;Lu, X.;Fang, Z.;Hu, Y.-S.;Zhou, J.;Chen, W.;Chen, L..LiNb_3O_8 as a novel anode material for lithium-ion batteries[J].Electrochemistry communications,201110(10):1127-1130. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%