通过共沉淀-热分解还原法，研究了一种容易实现的大规模制备 Fe-Ni 合金粉末的方法，根据质量守恒和同时平衡原理，建立了Ni2＋-Fe2＋-C2 O2－4-C2 N2 H8-H2 O 体系的热力学分析模型，并根据模型进行了相关计算，绘制了溶液中金属离子浓度对数-pH 图，系统研究了沉淀过程中溶液 pH 值对溶液中各离子浓度的影响.结果表明，当p H 值为3．5时，溶液中镍离子和亚铁离子的总浓度[Ni2＋]T、[Fe2＋]T达到一致，镍离子和亚铁离子的沉淀率相同，且沉淀基本完全，此时能够得到成分均匀性良好的 Fe-Ni 前驱体粉末.然后，将前驱体粉末在氢氩混合气氛中进行热分解还原，最终得到符合预期Ni/Fe摩尔比的合金粉末.
We have developed a facile strategy for the mass-production techniques of Fe-Ni alloy powder by a co-precipitation - thermal decomposition reduction method.According to the principle of simultaneous equilibrium and mass equilibrium,a series of thermodynamic equilibrium equations in the system at ambient temperature were deduced.The diagrams of logarithm ion concentrations versus pH values at different solution compositions were drawn based on the calculation results.The effects of pH value on the concentration of ions in solution were investigated.At about pH 3.5,the values of [Ni2+]T and [Fe2+]T were almost the same;the Ni2+ and Fe2+ were nearly completely precipitated,and the precipitation rate of these two type of ions were almost the same.Thus,homogeneous Fe-Ni alloys precursor can be obtained under such conditions.And then,the precur-sor was decomposed and reduced in flowing H2/Ar atmosphere.Finally,Fe-Ni alloy powders can be obtained.
参考文献
| [1] | Baicheng Zhang;Nour-Eddine Fenineche;Hanlin Liao;Christian Coddet.Microstructure and Magnetic Properties of Fe-Ni Alloy Fabricated by Selective Laser Melting Fe/Ni Mixed Powders[J].材料科学技术（英文版）,2013(8):757-760. |
| [2] | 张银亮;张传福;湛菁;黎昌俊;樊友奇.铁镍合金粉末的制备及应用现状[J].四川有色金属,2007(1):31-36. |
| [3] | Zhao, Y.;Sato, Y.S.;Kokawa, H.;Wu, A..Microstructure and properties of friction stir welded high strength Fe-36wt%Ni alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201125/26(25/26):7768-7773. |
| [4] | 黄小兵;陈红辉;周诗彪;杨基峰;张海涛.电镀Fe-Ni合金工艺的研究[J].电镀与环保,2014(4):32-34. |
| [5] | Geng, Yunlong;Ablekim, Tursunjan;Koten, Mark A.;Weber, Marc;Lynn, Kelvin;Shield, Jeffrey E..Defect generation and analysis in mechanically alloyed stoichiometric Fe-Ni alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2015:250-255. |
| [6] | Isao Matsui;Tomo Kawakatsu;Yorinobu Takigawa;Tokuteru Uesugi;Kenji Higashi.Fabrication of bulk nanocrystalline Fe-Ni alloys with high strength and high ductility by an electrodeposition[J].Materials Letters,2014Feb.1(Feb.1):71-74. |
| [7] | M.H.Xu;W.Zhong;X.S.Qi.Highly stable Fe-Ni alloy nanoparticles encapsulated in carbon nanotubes: Synthesis, structure and magnetic properties[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20101(1):200-204. |
| [8] | 张朝平;雷炳新;李振.W/O微乳液法制备Fe-Co-Ni合金和复合物纳米颗粒材料及其磁性能研究[J].纳米技术与精密工程,2012(1):36-45. |
| [9] | 张传福;姚永林;张银亮;湛菁.配位共沉淀-直接还原法制备超细纤维状铁镍合金粉[J].中国有色金属学报（英文版）,2012(12):2972-2978. |
| [10] | 孟祥东;李垚;赵九蓬;李雪;辛伍红.模板辅助电化学沉积三维有序大孔Fe-Ni合金膜[J].材料科学与工艺,2009(2):251-254. |
| [11] | Y. GAO;Z. Y. LI;D. JIN.Preparation and Characterization Alloy Powder by Chemical Co-Precipitation Hydrogen Reducing Process[J].Integrated Ferroelectrics,2011:54-58. |
| [12] | 湛菁;贺跃辉;周涤非;张传福.纤维状镍钴合金前驱体制备热力学分析与镍钴配比的控制[J].中国有色金属学报（英文版）,2011(5):1141-1148. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%